1) poly(trimethylene terephthalate)
聚对苯二甲酸丙二酯
1.
A kind of flame retardant and glass fiber reinforced poly(trimethylene terephthalate)(PTT) engineering plastic was prepared .
研制了一种30%玻纤增强阻燃聚对苯二甲酸丙二酯(PTT)工程塑料,重点考察了增韧剂、结晶成核剂、其它聚酯及溴锑复合阻燃剂对PTT性能的影响。
2.
Thermal spectra of poly(trimethylene terephthalate)(PTT) were collected over a temperature range of 40 ℃~250 ℃ by FT-IR micro-spectroscopy.
采用显微傅立叶转换红外光谱技术研究了聚对苯二甲酸丙二酯(PTT)的熔融相转变过程。
3.
The processes for solid state polymerization and glass fiber reinforcement of poly(trimethylene terephthalate)(PTT) were researched.
初步研究了聚对苯二甲酸丙二酯 (PTT)固相聚合及其玻璃纤维 (GF)增强工艺 ,探讨了PTT的热稳定性及GF含量和树脂特性粘度对GF增强PTT性能的影响 ,并对PTT与聚对苯二甲酸丁二酯 (PBT)增强前后的性能进行了比较。
2) polytrimethylene terephthalate
聚对苯二甲酸丙二酯
1.
The polytrimethylene terephthalate/polypropylene(PTT/PP 75/25) blend and its blend compatibilized by PP-g-MAH were prepared by melting blending method.
通过熔融共混制备了聚对苯二甲酸丙二酯/聚丙烯(PTT/PP=75/25)及其马来酸酐接枝PP(PP-g-MAH)增容共混物,研究了PTT/PP及其增容共混物的结晶性能、力学性能、流变性能和结晶形态。
2.
Capillary gas chromatography was applied to determine 1,3\|dipropylene glycol(DPG) in polytrimethylene terephthalate(PTT).
采用毛细管气相色谱法测定了聚对苯二甲酸丙二酯 ( PTT)产品中 1,3-二丙二醇 ( DPG)的含量 ,用乙醇胺降解法对 PTT大分子进行降解处理 ,选用了 CBP-W2 5 -10 0毛细管柱 ,氢火焰检测器 ,并用 1,6-己二醇作内标。
3.
Dimethyl terephthalate (DMT) and 1,3\|propanediol were selected as raw material to synthesize polytrimethylene terephthalate (PTT).
以对苯二甲酸二甲酯和 1 ,3-丙二醇为原料合成聚对苯二甲酸丙二酯 (PTT) ,重点研究了原料配比、缩聚温度、催化剂用量、稳定剂用量对聚合物粘度和端羧基含量的影响规律。
4) poly(trimethylene terephthlate)
聚对苯二甲酸丙二酯
1.
Decabromodiphenyl ethane(DBDPE),decabromodiphenyl oxide(DBDPO),and tris(tribro- mophenoxy)triazine(TBPC)were separately mixed with Sb_2O_3 and introduced into poly(trimethylene terephthlate)(PTT)through extrusion as flame retardants.
采用十溴二苯乙烷、十溴二苯醚和三(三溴苯氧基)三嗪分别与三氧化二锑复配,经双螺杆挤出机熔融共混制备阻燃聚对苯二甲酸丙二酯(PTT)复合材料,研究了阻燃剂的种类和用量对 PTT 结构性能的影响。
5) polytrimethylene terephthalate
聚对苯二甲酸丙二醇酯
1.
Investigation on the depolymerization of polytrimethylene terephthalate in methanol;
聚对苯二甲酸丙二醇酯的甲醇解聚研究
2.
The alloy of polycarbonate (PC)/polytrimethylene terephthalate (PTT) was modified with four different impact modifiers and compared with the imported PC/polybutylene terephthalate and PC/polyethylene terephthalate samples.
针对聚碳酸酯(PC)/聚对苯二甲酸丙二醇酯(PTT)共混合金相容性差的缺点,采用了4种不同的抗冲改性剂对其进行增韧改性,并与PC/聚对苯二甲酸丁二醇酯、PC/聚对苯二甲酸乙二醇酯进行性能比较。
3.
The melting behavior of polyethylene-2,6-naphthalate/polytrimethylene terephthalate(PEN/PTF)blends at different ratios was studied with a differential scanning calorimeter.
利用差示扫描量热仪对不同配比的聚萘二甲酸乙二醇酯/聚对苯二甲酸丙二醇酯(PEN/PTT)共混体系的熔融行为进行了分析,发现在共混体系中两组分形成各自的晶体,PEN和PTT的熔点均随另一组分含量的增加而下降。
6) poly(trimethylene terephthalate)
聚对苯二甲酸丙二醇酯
1.
Spinning Process of Poly(trimethylene terephthalate) Filament;
聚对苯二甲酸丙二醇酯长丝生产工艺
2.
The crystallization behavior of poly(trimethylene terephthalate) (PTT) containing various nucleation agents was studied by means of Differential Scanning Calorimetry (DSC), Depolarized Light Intensity(DLI) technique and Polarized Light Microscopy (PLM).
采用差示扫描量热(DSC)、解偏振光强度(DLI)和偏光显微镜(POM)等方法研究了含不同成核剂聚对苯二甲酸丙二醇酯(PTT)的结晶行为。
3.
Poly(trimethylene terephthalate)(PTT), a new material, is a promising polymer with potential applications.
新型聚酯材料聚对苯二甲酸丙二醇酯 (PTT)是一种极有应用潜力的聚合物 ,但在非纤维领域的研究与应用才刚开始。
补充资料：氨甲酸苯丙酯
分子式：C10H13NO2
分子量：179.21
CAS号：673-31-4
性质：白色有光泽的结晶性粉末。熔点101-104℃，溶于乙醇、氯仿、丙二醇及乙二胺，微溶于乙醚，几乎不溶于水。无臭，味微苦，稍有麻木感。
制备方法：由3-苯丙醇与氰酸钠缩合、水解而得。将无水甲苯、3-苯丙醇及氰酸钠加入反应罐中，冷至10℃，搅拌下导入氯化氢气体，约80min，温度上升至55℃后开始下降。通气毕，在55-60℃反应0.5h。冷至30℃，加入氨水升温至70℃，静置0.5h，分取有机层，过滤，滤液冷却结晶。过滤，结晶用甲苯洗涤，再用蒸馏水洗至氯根符合要求止。气流干燥，得苯丙氨酯。
用途：该品为枢骨胳肌松弛剂。用于肩、颈硬直，腰痛、四肢痛，运动后肌肉痛、扭挫伤、风湿性关节炎、神经痛及其他伴有痉挛等肌肉常紧张各症。
分子量：179.21
CAS号：673-31-4
性质：白色有光泽的结晶性粉末。熔点101-104℃，溶于乙醇、氯仿、丙二醇及乙二胺，微溶于乙醚，几乎不溶于水。无臭，味微苦，稍有麻木感。
制备方法：由3-苯丙醇与氰酸钠缩合、水解而得。将无水甲苯、3-苯丙醇及氰酸钠加入反应罐中，冷至10℃，搅拌下导入氯化氢气体，约80min，温度上升至55℃后开始下降。通气毕，在55-60℃反应0.5h。冷至30℃，加入氨水升温至70℃，静置0.5h，分取有机层，过滤，滤液冷却结晶。过滤，结晶用甲苯洗涤，再用蒸馏水洗至氯根符合要求止。气流干燥，得苯丙氨酯。
用途：该品为枢骨胳肌松弛剂。用于肩、颈硬直，腰痛、四肢痛，运动后肌肉痛、扭挫伤、风湿性关节炎、神经痛及其他伴有痉挛等肌肉常紧张各症。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条