1) C-Mn steel
碳锰钢
1.
Difference in grain growth between the submicron-sized and the micron-sized ferrite in C-Mn steels;
碳锰钢中亚微米和微米尺寸铁素体晶粒的长大行为
2.
The effect of deformation parameters,such as initial grain size,deformation temperature,strain rate and strain on dynamic recrystallization of C-Mn steel was investigated by means of single-hit compression tests.
采用单道次热模拟实验分析了各变形参数(初始晶粒尺寸、变形速率、变形温度和变形量)对碳锰钢动态再结晶的影响。
2) medium carbon steel containing manganese
中碳锰钢
1.
This paper analyses the characteristic of medium carbon steel containing manganese and the demand to casting powder.
通过对中碳锰钢钢种特点及其对保护渣要求的深刻剖析,结合包钢的生产实际,对方、圆坯中碳锰钢生产所用保护渣的使用性能和理化性能进行了综合分析研究。
3) low carbon manganese steel
低碳锰钢
1.
Influences of deformation parameters on microstructures and mechanical properties of low carbon manganese steel
变形制度对低碳锰钢组织性能的影响
2.
Controlled rolling and controlled cooling experiments under various technology parameters have been carried out on low carbon manganese steels.
在实验室对低碳锰钢进行了控轧控冷试验。
3.
Thermo-mechanical controlled process (TMCP) experiments with finish-rolling temperatures (FRT) higher than Ar3 and different coiling temperatures (CT) have been carried out on a low carbon manganese steel.
对一种低碳锰钢进行了终轧温度高于Ar3卷取温度的不同控轧控冷处理。
4) carbon manganese steel
低锰碳钢
5) high carbon and high manganese steel
高碳锰钢
6) High Manganese Carbon Steel
高锰碳钢
补充资料：锰钢
分子式：
CAS号：
性质：含有一定量锰的钢。锰是良好的脱氧剂和脱硫剂。一定数量的锰能减弱钢因硫所引起的热脆性，可改善钢的热加工性。锰和铁形成固溶体，提高钢中铁素体和奥氏体强度。它又是碳化物形成元素，进入渗碳体中取代一部分铁原子。锰降低临界转变温度从而使珠光体细化、强化。锰扩大r相区，形成奥氏体组织能力仅次于镍。它强烈增加钢的淬透性。含锰量较高的钢有晶间粗化倾向，增加钢的回火敏感性。
CAS号：
性质：含有一定量锰的钢。锰是良好的脱氧剂和脱硫剂。一定数量的锰能减弱钢因硫所引起的热脆性，可改善钢的热加工性。锰和铁形成固溶体，提高钢中铁素体和奥氏体强度。它又是碳化物形成元素，进入渗碳体中取代一部分铁原子。锰降低临界转变温度从而使珠光体细化、强化。锰扩大r相区，形成奥氏体组织能力仅次于镍。它强烈增加钢的淬透性。含锰量较高的钢有晶间粗化倾向，增加钢的回火敏感性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。