1) Mullite-corundum castables
莫来石-刚玉浇注料
1.
Mullite-corundum castables were prepared with sintered mullite(w(Al2O3)>45%),fused mullite(w(Al2O3)>70%),corundum(w(Al2O3)>99%),α-Al2O3 micropowder(w(Al2O3)>99.
0%)等为主要原料,制备了莫来石-刚玉浇注料试样,经110℃24 h、1 000℃3 h和1 400℃3 h处理,研究了ρ-Al2O3加入量(w)分别为1%、2%、3%、4%和5%对莫来石-刚玉浇注料性能的影响。
2.
Mullite-corundum castables for desulphurizing lance were prepared using mullite M45(10～5 mm,5~3 mm),fused mullite(3~1 mm,≤1 mm)as aggregates,and corundum powder(≤0.
07μm)作基质,制备了脱硫枪用莫来石-刚玉浇注料,并分别研究了SiO2微粉加入量(分别为2%、3%、4%、5%)和Al2O3微粉加入量(分别为2%、4%、6%)对浇注料体积密度、显气孔率、强度、烧后永久线变化率、抗热震性和抗渣性的影响。
3) mullite-corundum materials
莫来石-刚玉材料
1.
In this paper, andalusite, kyanite and sillimanite were added to mullite-corundum materials and the effect of andalusite, kaynite and sillimanite on properties of mullite-corundum materials was studied.
首先，研究了红柱石的粒度和加入量对莫来石-刚玉材料性能的影响。
4) mullite cast refractory
莫来石浇注料
1.
The life campaign of the furnace top lining will be lasted by using mullite cast refractory with high strength and alumina and carrying out construction carefully and drying correctly.
阐述了加热炉炉顶耐火材料烧损机理 ,通过选择高强高铝莫来石浇注料作为炉衬 ,精心组织施工 ,科学烘炉达到了延长炉顶使用寿命的目的。
2.
The campaign life of the furnace top lining will be lasted by using Mullite cast refractory with high strength and alumina and by carrying out construction carefully and drying correctly.
阐述了加热炉炉顶耐火材料烧损机理 ,通过选择高强高铝莫来石浇注料作为炉衬 ,精心组织施工 ,科学烘炉达到了延长炉顶使用寿命的目
5) corundum-mullite materials
刚玉-莫来石
1.
The effect of NaF on the synthesis of corundum-mullite materials from high aluminum fly ash;
NaF对高铝粉煤灰合成刚玉-莫来石材料的影响
2.
In this paper,the influence of temperature and Li2O on the properties,crystal structure,and morphology of corundum-mullite materials prepared from fly ash and bauxite was studied.
研究了Li2O、烧结温度对高铝粉煤灰和铝矾土合成刚玉-莫来石材料的性能、物相组成和显微结构的影响。
6) corundum-mullite
刚玉莫来石
1.
Effects of micro-powder and firing temperature on microstructure and properties of corundum-mullite materials;
微粉及烧成温度对刚玉莫来石材料结构的影响