1) titania-ceria composite films
二氧化钛-二氧化铈复合薄膜
2) nanometer TiO_2 composite thin films
纳米二氧化钛复合薄膜
4) TiO2/porous Ti composite membrane
二氧化钛/多孔钛复合膜
1.
The results showed that the TiO2/porous Ti composite membranes,which were dip-coated more than three times,could be inhibited the passage of immunoglobulin and immune cells.
实验结果显示,所制得的二氧化钛/多孔钛复合膜经过3次以上涂膜能有效地阻隔免疫球蛋白及免疫细胞,但小分子物质(如葡萄糖)能自由通过该膜,故该复合膜可以作为免疫隔离膜使用,并且具有良好的免疫隔离效果。
5) TiO2 thin film
二氧化钛薄膜
1.
Coating the TiO2 Thin Film on the Active Carbon with CVD and Photo-Catalytic Degradation of Acid Violet Red;
用CVD法在活性炭上镀二氧化钛薄膜光催化降解酸性品红
2.
The results show that TiO2 fine particle appeared anatase structure in TiO2 thin films,and formed the composite phase structure of anatase,rutile and Brookit of TiO2 powders.
实验结果表明:溶胶的陈化时间、膜的热处理温度、涂膜层数等都将直接影响二氧化钛薄膜的紫外可见光谱和禁带宽。
6) titania film
二氧化钛薄膜
1.
The results of SEM and TF-XRD indicate that a titania film layer with anatase and rutile structure was formed on the surface of NiTi SMA after oxidized with hydroxyl radical (·OH) as an oxidant.
通过高级氧化法对NiTi形状记忆合金进行表面改性,SEM和TF-XRD分析证实,羟自由基(·OH)氧化后的NiTi形状记忆合金表面生成了金红石和锐钛矿结构的二氧化钛薄膜。
补充资料：复合薄膜
由两层或多层不同材料的薄膜复合而成的高分子材料，主要用于包装。通过复合，可以获得具有各单一材料综合性质的材料，使用的基材主要有塑料薄膜（如聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯和聚酯等）、玻璃纸、纸张和金属箔等。基材的复合可以采用挤出复合方法或借助于胶粘剂进行胶粘复合。
以聚乙烯为例。其挤出复合方法(图1)是将聚乙烯投入料斗，经过挤出机从细缝挤出一定厚度熔融膜，与送入的基材在压力滚筒和冷却滚筒之间复合、卷取，即得制品。从冷却滚筒引入第二基材，可制得聚乙烯夹心的三层复合膜；如在该复合膜两侧再复以聚乙烯，即可得五层复合膜。这种聚乙烯复合薄膜的用途相当广泛（见表）。
多层塑料复合薄膜也可采用共挤出方法(见挤出)制得。采用几台挤出机分别将几种不同的树脂引入一公共机头中，然后从口模中挤出，即得制品。
借助胶粘剂制取多层复合薄膜(图2)的装置是将胶粘剂用涂布机涂敷在薄膜或其他基材上，在干燥区干燥，然后与其他基材热压复合。基材涂敷胶粘剂后亦可先与其他基材复合，然后干燥。
以聚乙烯为例。其挤出复合方法(图1)是将聚乙烯投入料斗，经过挤出机从细缝挤出一定厚度熔融膜，与送入的基材在压力滚筒和冷却滚筒之间复合、卷取，即得制品。从冷却滚筒引入第二基材，可制得聚乙烯夹心的三层复合膜；如在该复合膜两侧再复以聚乙烯，即可得五层复合膜。这种聚乙烯复合薄膜的用途相当广泛（见表）。
多层塑料复合薄膜也可采用共挤出方法(见挤出)制得。采用几台挤出机分别将几种不同的树脂引入一公共机头中，然后从口模中挤出，即得制品。
借助胶粘剂制取多层复合薄膜(图2)的装置是将胶粘剂用涂布机涂敷在薄膜或其他基材上，在干燥区干燥，然后与其他基材热压复合。基材涂敷胶粘剂后亦可先与其他基材复合，然后干燥。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。