1) critical pitting temperature
临界点蚀温度
1.
The influence of concentration of fluoride ion on the pitting corrosion behavior of 316SS has been investigated by means of measuring the critical pitting temperature (CPT) in 0.
用电化学测量临界点蚀温度(CPT)的方法,研究0。
2.
And the critical pitting temperature(CPT) was measured.
采用外加恒定电位下腐蚀电流-温度扫描的方法分别研究了304、316不锈钢在不同浓度NaC l水溶液中的临界点蚀温度。
3.
According to ASTM G48 standard test method,we tested the critical pitting temperature(CPT) on 2205 duplex stainless steel used in some nature gas pipeline projects and studied the phenomenon and reason of pitting.
依据ASTM G48标准试验方法对某天然气管道工程应用的2205双相不锈钢钢管的临界点蚀温度进行了测定,并且对产生点蚀的现象和原因进行了研究。
2) critical temperature point
温度临界点
1.
This article illuminates the existence of a critical temperature point in the changing process of thin films structure and properties from the theoretical perspective.
本文先从理论角度说明了薄膜结构性能变化中存在“温度临界点”,然后借助于XRD、Ram an等测试仪器研究分析了S i薄膜、AZO薄膜在晶化过程、晶粒长大过程以及性能突变中的“温度临界点”。
3) critical temperature
临界点温度
1.
A simulation calculation of the critical temperature of 2D Ising model;
二维伊辛模型相变临界点温度的模拟计算
4) thermal critical point
热临界点，临界温度
5) tricritical properties
三临界点温度
6) critical point in material corrosion
腐蚀临界点
补充资料：点蚀
分子式：
CAS号：
性质：又称坑蚀，斑点腐蚀，小孔腐蚀或点蚀。金属表面大部分区域腐蚀相对较轻，而某些局部出现向纵深发展的腐蚀小孔的腐蚀形态。孔蚀的原因是活性阴离子导致表面钝化膜局部破坏。具有钝化能力的金属如不锈钢、铝合金及碳钢等，在含氯离子介质中经常发生孔蚀。蚀孔的发展速度有时很快，可以深入金属甚至短时间内蚀穿金属截面，且较难预测，因此孔蚀往往比均匀腐蚀具有更大的危害性。可以通过降低介质中的有害阴离子浓度，采用涂层保护、添加缓蚀剂和阴极保护等方法予以减轻或防止。