1) sulfate leaching solution
硫酸浸出液
1.
The enrichment and the purification of copper from a simulated sulfate leaching solution of low grade copper ore with SP-C resin,a novel silicagel-polyamine composite chelating resin,were studied.
研究SP-C硅胶-聚合胺树脂在模拟低品位铜矿硫酸浸出液中富集纯化铜的工艺,在Cu2+1~2 g/L、Fe3+2~8 g/L范围内,考察该树脂吸附分离铜铁的性能。
2) sulfuric acid leach
硫酸浸出
1.
The paper,according to the analyzing of lead dross reverberator dust,put forward the new technics indium distilling by sulfuric acid leaching,P204 extraction,sulfuric acid washing,hydrochloric acid reverse extraction,zinc replacement,smelting,electrolysis,casting etc.
研究分析了铅浮渣反射炉烟尘的性质和特点,提出了二段硫酸浸出、P204萃取、硫酸洗涤、盐酸反萃、锌板置换、压团熔铸、电解铸型的提铟新工艺,并进行了全流程的试验研究,明确了各工序的工艺技术条件。
3) sulfuric acid leaching
硫酸浸出
1.
Thermodynamic analysis results show that tellurium can be leached by sulfuric acid leaching method from lead-rich tellurium slag.
并通过硫酸浸出高铅碲渣中碲的条件实验验证了热力学分析的结果。
2.
In this paper, the method of preparation of amorphous silica from serpentine and bentonite by sulfuric acid leaching in microwave field was investigated.
本文研究了微波辐照作用下，由蛇纹石、膨润土硫酸浸出制备无定形二氧化硅的方法；考查了反应时间、微波辐照强度、液固比、硫酸浓度、矿石粒度等因素对矿物浸出过程的影响；确定了酸浸最佳工艺条件；分析了制得的无定形二氧化硅的化学组成；研究了微波作用下蛇纹石的硫酸浸出动力学。
3.
Therefore, research on sulfuric acid leaching of high silica zinc oxide ore focuses on how to improve filtration performance of ore pulp.
氧化锌矿通常含SiO_2较高，直接酸浸时溶出的SiO_2容易致使矿浆固液分离困难，如何改善矿浆的过滤性能是高硅氧化锌矿硫酸浸出工艺研究的重要内容。
4) leaching by sulfuric acid
硫酸浸出
1.
Hydrated aluminium sulfate(Al_2(SO_4)_3·18H_2O) were prepared by activating,magnetic separation,leaching by sulfuric acid,leaching by hot water,crystallization processes using fly ash and sulfuric acid as raw materials.
以粉煤灰和硫酸为原料,经活化、磁选、硫酸浸出、硫酸铝溶出、结晶制备出Al2(SO4)3。
5) sulfuric acid leached liquor
硫酸浸液
1.
On the basis of thermodynamics theory,and according to the content of Fe3+ in sulfuric acid leached liquor from waste Mn-Zn ferrite powders and the theoretical prescription of Mn-Zn ferrite,the sulfuric leached liquors’ proportion reduction processes,in which special proportion reducing agents of Fe,Mn and Zn powders were used,were studied.
在热力学理论分析的基础上,依据锰锌铁氧体废料硫酸浸液中Fe3+的量及铁氧体理论配方,研究利用金属铁粉、锰粉和锌粉对此浸出液的定比例还原过程。
6) acid leaching liquor
酸浸出液
1.
A solvent extraction process using P,,,-kerosene-H,SO' extraction system for separa-tion of Fe3+ from sulfuric acid leaching liquor of electroplating sludge was studied.
研究了采用P507-煤油-H2SO4萃取体系分离电镀污泥酸浸出液中Fe3＋的工艺，确定了从含有多种金属组分的硫酸溶液中萃取铁的最佳工艺条件以及负载有机相反萃取较优工艺条件。
补充资料：硫酸卡那霉素注射液
【通用名称】
硫酸卡那霉素注射液
【其他名称】
硫酸卡那霉素注射液 硫酸卡那霉素注射液 拼音名：Liusuan Kanameisu Zhusheye 英文名：Kanamycin Sulfate Injection 书页号：2000年版二部－417 本品为硫酸卡那霉素的灭菌水溶液。按卡那霉素(C18H36N4O11) 计算，应为标示量 的90.0％～110.0 ％。
【性状】
本品为无色、微带黄色或黄绿色的澄明液体。
【鉴别】
取本品，照硫酸卡那霉素项下的鉴别试验，显相同的结果。
【检查】
pH值 应为4.5 ～7.5 （附录Ⅵ H）。 颜色 本品应无色；如显色，与黄色或黄绿色4号标准比色液（附录Ⅸ A第 一法）比较，不得更深。 无菌 取本品，分别加入100ml 0.9％无菌氯化钠溶液中，用薄膜过滤法处理后， 依法检查，（附录Ⅺ H），应符合规定。 异常霉性、热原与降压物质 照硫酸卡那霉素项下的方法检查，均应符合规定。 其他 应符合注射剂项下有关的各项规定（附录Ⅰ B）。
【含量测定】
精密量取本品适量，照硫酸卡那霉素项下的方法测定。
【类别】
同单硫酸卡那霉素。
【规格】
2ml:0.5g（50万单位）
【贮藏】
密闭保存。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条