1) PTFE/PA66 blends
PTFE/PA66共混物
1.
The effects of PTFE content on water-absorptivity,notched impact strength and complex viscosity of PTFE/PA6 and PTFE/PA66 blends were investigated by water immersion test,Charpy impact fracture test and dynamic rheology measurement in this paper.
通过浸水实验、缺口冲击断裂实验和动态流变测试,考察了PTFE含量对PTFE/PA6和PTFE/PA66共混物的吸水率、冲击断裂强度及熔体黏度的影响以及熔体黏度随温度和频率的变化规律。
2) PA66/PTFE blends
PA66/PTFE共混物
1.
PA6/PTFE and PA66/PTFE blends with different PTFE contents are prepared by melt blending in twin-screw extrusion process, in which PA6 and PA66 are the continuous phase and PTFE is the dispersed phase.
本工作以PA6和PA66为连续相,以PTFE为分散相,采用双螺杆挤出熔融共混技术制备了不同比率的PA6/PTFE和PA66/PTFE共混物,利用60Co-γ射线源,以不同辐照剂量(20kGy、50kGy和100kGy)对这两个材料体系进行了γ辐照。
3) PA66/LLDPE blends
PA66/LLDPE共混物
4) PA66/PP blend
PA66/PP共混物
1.
The influence of POE-MAH on the morphological structure and the compatibilily of PA66/PP blends was studied by SEM, DSC and WAXD.
通过扫描电镜(SEM)观察、差示扫描量热法(DSC)和广角X射线衍射分析(WAXD),研究了POE-MAH对PA66/PP共混物的形态结构和相容性的影响。
5) PET/PA66 Blends
PET/PA66共混物
6) PA66/irradiated LLDPE blends
PA66/辐照LLDPE共混物
补充资料：nylon 66 salt
分子式：H3N(CH2)6NH3COO(CH2)4COO
CAS号：
性质：又称尼龙-66盐。无色结晶性粉末。熔点(192±2)℃。能溶于水。微溶于乙醇。由己二酸和己二胺中和制得。生产聚酰胺66纤维的单体，熔融温度为197～198℃的白色结晶粉末。在加压和加热的条件下即可缩聚制得聚酰胺66。另外，ε-己内酰胺也是尼龙盐，可用其制得聚酰胺6。也是生产尼龙-66树脂的原料，用于合成纤维和塑料工业。
CAS号：
性质：又称尼龙-66盐。无色结晶性粉末。熔点(192±2)℃。能溶于水。微溶于乙醇。由己二酸和己二胺中和制得。生产聚酰胺66纤维的单体，熔融温度为197～198℃的白色结晶粉末。在加压和加热的条件下即可缩聚制得聚酰胺66。另外，ε-己内酰胺也是尼龙盐，可用其制得聚酰胺6。也是生产尼龙-66树脂的原料，用于合成纤维和塑料工业。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条