A kind of typical thermoplastic elastomer—ethylene vinyl acetate(EVA) was chosen as the study subject.
本文在深入研究了乙烯-醋酸乙烯共聚物(EVA)材料特性和粉碎机理的基础上,将空气涡轮制冷低温粉碎技术应用于EVA低温细碎中,有效地提高了EVA颗粒的超细粉碎效率;同时指出了该粉碎流程的关键技术及影响粉碎效果的主要因素,开辟了一条规模化、高质量、低能耗回收可再生塑料的新途径。
2.
The EVA and starch were extruded by extruser and the controlled-release matrix of quinclorac was prepared.
以淀粉和乙烯-醋酸乙烯共聚物(EVA)为原料,采用螺杆挤出工艺,制备一种可生物降解的淀粉/EVA复合基材,用作除草剂3,7-二氯喹啉-8-羧酸的控制释放。
3.
A foamed plastics product was prepared from SEBS,LDPE and EVA.
将苯乙烯-乙烯/丁烯-苯乙烯共聚物(SEBS)应用于低密度聚乙烯(LDPE)/乙烯-醋酸乙烯共聚物(EVA)发泡材料中。
6) ethylene vinyl-acetate copolymer
乙烯/醋酸乙烯酯共聚物
1.
The photocrosslinking of ethylene vinyl-acetate copolymer (EVA) containing phosphorus- nitrogen halogen-free flame retardant (EM82) was studied,It found that the EVA/EM82 samples with a thickness of 1.
对磷氮类阻燃剂(EM82)无卤阻燃乙烯/醋酸乙烯酯共聚物(EVA)复合材料进行了紫外光交联研究。
补充资料：VAE emulsion
VAE乳液是醋酸乙烯与乙烯经乳液聚合而得的共聚物水分散体系。乳白色粘稠液体，固含量50%～55％，粘度200～3300mPas，PH值4～5. 5，最低成膜温度-3～l 0℃，玻璃化温度Tg＝-3～7℃，表面张力30mN／m。
在VAE乳液的分子中，由于乙烯基的引入使得高分子主链变得柔软，具有内增塑作用，避免了外加低分子量增塑剂产生的迁移、渗出、挥发等缺点。最低成膜温度和玻璃化温度降低。对氨、臭氧和紫外线都很稳定，耐酸碱性、耐冻融性、贮存稳定性均优于PvAc乳液。具有较低的表面张力，对薄膜材质有特殊的粘接性。有很好的湿粘性和很快的固化速度。耐碱性、抗蠕变性优于丙烯酸酯乳液。较好的耐水性、耐高温性，在250℃下不分解。 ·
VAE乳液是一种应用广泛的乳液粘合剂，能够粘接木材、纸品、织物、皮革、混凝土、镀锌钢板、铝箔等，特别适宜粘接PVC、聚酯、尼龙、玻璃纸等薄膜．还可用VAE乳液配制无纺布胶粘剂、PVC复膜胶粘剂、高强耐水白乳胶、高速卷烟胶粘剂、地毯胶粘剂、压敏胶粘剂、热封胶粘剂、建筑胶粘剂。也可用VAE乳液作为种子，与其他单体进行聚合形成复合乳液，如VAE／MMA复合乳液。
在VAE乳液的分子中，由于乙烯基的引入使得高分子主链变得柔软，具有内增塑作用，避免了外加低分子量增塑剂产生的迁移、渗出、挥发等缺点。最低成膜温度和玻璃化温度降低。对氨、臭氧和紫外线都很稳定，耐酸碱性、耐冻融性、贮存稳定性均优于PvAc乳液。具有较低的表面张力，对薄膜材质有特殊的粘接性。有很好的湿粘性和很快的固化速度。耐碱性、抗蠕变性优于丙烯酸酯乳液。较好的耐水性、耐高温性，在250℃下不分解。 ·
VAE乳液是一种应用广泛的乳液粘合剂，能够粘接木材、纸品、织物、皮革、混凝土、镀锌钢板、铝箔等，特别适宜粘接PVC、聚酯、尼龙、玻璃纸等薄膜．还可用VAE乳液配制无纺布胶粘剂、PVC复膜胶粘剂、高强耐水白乳胶、高速卷烟胶粘剂、地毯胶粘剂、压敏胶粘剂、热封胶粘剂、建筑胶粘剂。也可用VAE乳液作为种子，与其他单体进行聚合形成复合乳液，如VAE／MMA复合乳液。