1) two-step hot-dipping process
热浸双镀工艺
3) hot dip process
热浸工艺
1.
In hot dip 55%Al Zn alloy cladding of steel sheet by passivation method, the effects of concentration of passivant, passivation treatment and hot dip processes on the cladding thickness and quality are strdied by orthogonal designed test in this paper.
用正交试验法研究了钝化法热浸镀中钝化剂浓度、钝化工艺、热浸工艺对钢板热浸镀55% Al- Zn合金镀层厚度和质量的影响 ,得出了获得良好质量镀层的最佳钝化条件和热浸工
4) hot-dip galvanizing technique
热浸锌工艺
1.
Through brief introduction of hot-dip galvanizing technique, this pa per analyses on each process's target, methods and requirements and, based on th e standard requirements and features of waveform guardrail, puts forward some pr oblems needing attention in hot-dip galvanizing technique and decisive factors influencing the working life of galvanizing boiler.
通过扼要介绍热浸锌工艺,分析了各工序的目的、方法及要求,并针对波型梁护栏的标准要求及特点,提出在热浸锌工艺中应注意的问题及影响镀锌锅寿命的决定性因素。
5) Thermovinification
热浸渍工艺
6) extraction of hot water
热浸提工艺
补充资料：热浸镀
分子式：
CAS号：
性质：又称熔融镀（fuse dipping）。将工件浸入熔融的金属液中，以获得金属镀层的过程。能用于热浸镀的金属只是熔点较低的金属及其合金。如锡、锌、铝、铅锡合金等。基体材料一般是钢铁，有时也用铜。浸镀前工件需进行表面预处理，清除表面的油污和氧化皮。热浸镀后还要进行化学处理、涂油或必要的整形。热浸镀的优点在于得到的镀层较厚，能在较恶劣的环境中长期使用。如用于高速公路的护栏、桥梁和建筑材料。但浸镀层厚度和均匀性不易控制，外观也不如电镀层好。优点是：（1）操作和设备简单；（2）效果比电镀好。缺点是：（1）覆盖层较厚；（2）不规则的制件不容易形成均匀的膜；（3）只适于用低熔点金属（锌、锡、铝、铅）覆盖。
CAS号：
性质：又称熔融镀（fuse dipping）。将工件浸入熔融的金属液中，以获得金属镀层的过程。能用于热浸镀的金属只是熔点较低的金属及其合金。如锡、锌、铝、铅锡合金等。基体材料一般是钢铁，有时也用铜。浸镀前工件需进行表面预处理，清除表面的油污和氧化皮。热浸镀后还要进行化学处理、涂油或必要的整形。热浸镀的优点在于得到的镀层较厚，能在较恶劣的环境中长期使用。如用于高速公路的护栏、桥梁和建筑材料。但浸镀层厚度和均匀性不易控制，外观也不如电镀层好。优点是：（1）操作和设备简单；（2）效果比电镀好。缺点是：（1）覆盖层较厚；（2）不规则的制件不容易形成均匀的膜；（3）只适于用低熔点金属（锌、锡、铝、铅）覆盖。