1) crystal adhesive
水晶胶
1.
Factors affecting gelation time of crystal adhesive for decorations;
影响饰品用水晶胶凝胶时间的因素
2) Hydrogel intraocular lens
水凝胶人工晶体
3) polyester resin
水晶胶 聚酯树脂
4) polyester resin
聚酯树脂 水晶胶
5) Colloid crystal
胶晶
1.
Three-Dimentionally Ordered macroporous titanium-silica mixed oxides were successfully synthesized by using polystyren sphere colloid crystal as the template and the sol of tetraethyl silicate and tetrabutoxy-titane as the filling fluid.
以聚苯乙烯微球离心后形成的三维规则排列的胶晶作模板,用钛酸丁酯和正硅酸乙酯分别和水、乙醇等配制成的混合溶胶填充微球之间的间隙,然后原位形成凝胶,最后通过焙烧(<5℃/min;300℃,5h;570℃,5～10h,空气流速1L/min)除去微球得到三维规则排列的大孔钛硅混合氧化物。
2.
Three dimensionally ordered macroporous silica was successfully synthesized using latex sphere colloid crystal as template and sol of tetraethyl orthosilicate, water, ethanol and hydrochloric acid as filling fluid.
以聚苯乙烯微球离心后形成的三维规则排列的胶晶作模板 ,以正硅酸乙酯、水、乙醇和盐酸等配制的溶胶填充微球间的间隙 ,然后原位形成凝胶 ,最后通过焙烧除去微球得到三维规则排列大孔二氧化硅材料 。
3.
Periodic macroporous titanium dioxide were successfully synthesized using PS colloid crystal as templates which were made by centrifuging latex sphere, filling in the voids with sol of terabutoxy_titane, and then transforming into gel in situ and removing latex sphere by calcinations.
以聚苯乙烯微球 (LatexSphere)离心后形成的三维规则排列的胶晶 (colloidcrystal)作模板 ,用钛酸丁酯、水、乙醇等配制的溶胶填充微球之间的间隙 ,然后原位形成凝胶 ,最后通过焙烧除去微球得到三维规则排列大孔TiO2 材料 (3DOM)。
6) colloidal crystal
胶晶
1.
Polystyrene colloidal crystals were assembled by natural sedimentation,centrifugation and vertical deposition methods.
采用自然沉降法、离心法和垂直沉积法组装了聚苯乙烯胶晶。
2.
Polystyrene colloidal crystal films(PCCF) were assembled by vertical deposition method.
采用垂直沉积法组装了三维聚苯乙烯胶晶膜,并用其为模板制备了三维有序大孔(3DOM)SiO2膜。
补充资料：Sds-聚丙烯酰胺凝胶电泳凝胶电泳
sds-聚丙烯酰胺凝胶电泳（sds-page，sodium dodecyl sulfate-polyacrylamide gel electrohoresis）
在有去污剂十二烷基硫酸钠存在下的聚丙烯酰胺凝胶电泳。sds-page只是按照分子大小分离的，而不是根据分子所带的电荷和大小分离的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条