The optimum process conditions of surface modification of wollastonite were suggested as follows: modification reagent stearic acid,modification reagent dosage 2%,modification time 15～20 min,modification temperature 70 ℃.
通过对超细硅灰石粉体的表面化学改性效果的研究,确定了最佳工艺条件:改性剂为硬脂酸,改性剂用量2%,改性时间15~20min,改性温度70℃。
4) Surface Chemical Modification
表面化学改性
1.
The surface chemical modification of ultrafine sericite was carried out by using silane coupling agent.
采用硅烷偶联剂对超细绢云母进行表面化学改性 ,通过对径厚比、改性绢云母填充量等变量的研究 ,探讨改性绢云母增强尼龙 6力学性能的变化规律 。
2.
With natural minerals as raw materials, silicone rubber reinforcement fillers, namely the modified ultrafine powders with excellent properties, are prepared through ultrafine crashing, surface chemical modification and mechanical chemical modification.
以天然矿物滑石、石英、粒状硅灰石和针状硅灰石为原料，经超细粉碎、表面化学改性和机械力化学改性等三种工艺方法进行深加工，制备出具有优良性能的超细粉体材料———硅橡胶增强填料，其性能接近气相白碳黑，可部分代替白碳黑用于硅橡胶。
3.
With ultrafine crashing and surface chemical modification, hard|sericite was modified.
采用超细粉碎和表面化学改性方法对硬质绢云母进行改性 ,研究表面改性的机理 ,建立了一整套的改性工艺 ,制备出应用性能和价值得到较大提高的改性硬质绢云母超细粉。
5) surface chemical modificated activated carbon
表面化学改性活性炭
1.
Application of surface chemical modificated activated carbon that in water treatment;
表面化学改性活性炭在水处理中的应用
6) surface in-situ chemistry multi-modification
表面原位化学组合改性
补充资料：熔盐电化学表面合金化
分子式：
CAS号：
性质：其实质是熔盐中金属的电沉积和固态扩散合金化两种作用的综合。当在熔盐中使用活性较强的金属作为阳极，以活性较弱的金属作为阴极，并将阴、阳极连成回路，则形成一个自发的原电池。阳极在熔盐中溶解，其离子在阴极表面放电析出。与此同时，于高温下在基体（阴极）表面沉积的合金元素向内部扩散形成固溶体或金属间化合物的表面合金层。通过改变基体金属和被沉积金属，可以获得具有特殊性质的表面合金，性质远优于单个金属。铌、钽、铝、铍、硅等的表面合金化已在高技术领域中得到了应用。
CAS号：
性质：其实质是熔盐中金属的电沉积和固态扩散合金化两种作用的综合。当在熔盐中使用活性较强的金属作为阳极，以活性较弱的金属作为阴极，并将阴、阳极连成回路，则形成一个自发的原电池。阳极在熔盐中溶解，其离子在阴极表面放电析出。与此同时，于高温下在基体（阴极）表面沉积的合金元素向内部扩散形成固溶体或金属间化合物的表面合金层。通过改变基体金属和被沉积金属，可以获得具有特殊性质的表面合金，性质远优于单个金属。铌、钽、铝、铍、硅等的表面合金化已在高技术领域中得到了应用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条