1) PVC/SAN blends
PVC/SAN共混物
1.
Effect of AN content on the compatibility of PVC/SAN blends;
AN含量对PVC/SAN共混物相容性的影响
2) SAN/PMMA blend
SAN/PMMA共混物
3) PVC/ABS blend
PVC/ABS共混物
1.
The effect of plasticizer dioctyl phthalate(DOP) on the mechanical properties and shore A handness of PVC (SG-3,SG-5) and PVC/ABS blend were stuided.
研究了增塑剂DOP对聚氯乙烯(商品牌号SG-3,SG-5)及PVC/ABS共混物力学和硬度等性质的影响及其机理。
4) poly (vinyl chloride) /methylnethacrylacte-butadiene-styrene blend
PVC/MBS共混物
5) PMSQ/PVC blends
PMSQ/PVC共混物
6) ABS/PVC blends
ABS/PVC共混物
1.
The mechanical and theological properties of ABS/PVC blends are studied and the effects of compatibilizer α-SAN on the mechanical properties of ABS/PVC alloy are also discussed.
本文研究了ABS/PVC共混物的物理力学性能和加工流动性,并讨论了相容剂α-SAN对ABS/PVC共混物力学性能的影响。
补充资料：PVC/SAN blend
分子式：
CAS号：
性质：系由聚氯乙烯添加丙烯腈-苯乙烯共聚物组成的共混物，SAN共聚物可改善聚氯乙烯的加工性能和耐热性能，提高塑化速度，加入SAN共聚物，可使塑化时间从>30min降为2.5min，拉伸屈服强度可由41.63MPa提到55.28MPa，缺口冲击强度由24.8kJ/m2提高到37.3kJ/m2；制成薄壁制品的透明性好，收缩率低。用机械共混法制备。可用于热水管、异型材及其他注射件方面。
CAS号：
性质：系由聚氯乙烯添加丙烯腈-苯乙烯共聚物组成的共混物，SAN共聚物可改善聚氯乙烯的加工性能和耐热性能，提高塑化速度，加入SAN共聚物，可使塑化时间从>30min降为2.5min，拉伸屈服强度可由41.63MPa提到55.28MPa，缺口冲击强度由24.8kJ/m2提高到37.3kJ/m2；制成薄壁制品的透明性好，收缩率低。用机械共混法制备。可用于热水管、异型材及其他注射件方面。