1) porous silica
多孔SiO2
1.
Unconsidering the effect of crossing factors,a series experiments with 5-factor and 4-level experiments are designed to study on the effect to diameter of porous silica particles prepared from wollastinite.
在不考虑交互作用情况下,设计了五因素四水平正交实验以考察诸因素对硅灰石制多孔SiO2聚集体颗粒粒径的影响。
2.
This paper reported the study on surface treatment of porous silica by the means of chemistry, microwave and plasma and etc.
通过化学方法、微波照射以及空气等离子体处理对多孔SiO2 表面进行了激活 ,再将激活了的SiO2 进行表面水合 。
3.
Low dielectric constant thin film of nanoporous silica synthesized by sol-gel w as deposited on Si(100) substrate by spin coating.
以正硅酸乙酯 (TEOS)为原料 ,采用旋转涂敷的方法 ,结合溶胶 凝胶技术在硅衬底上制备超低介电常数多孔SiO2 薄膜 采用两种不同的改性方法对薄膜表面进行改性 ,傅里叶变换红外光谱分析发现改性后薄膜中含有大量的—CH3键 ,从而减少了孔洞塌陷 。
2) porous SiO2
多孔SiO2
1.
Mesoporous SiO2 monoliths with pore diameter of ~20 nm for enzyme immobilization were synthesized via sol-gel route by using tetraethoxysilane (TEOS), polyethylene glycol (PEG) and gelatin as raw materials.
本文通过溶胶-凝胶法,以正硅酸乙酯、聚乙二醇和明胶为主要原料,制得了孔径约为20nm的生物酶载体用多孔SiO2块状材料,并着重研究了热处理温度对多孔SiO2载体的结构和酶活力的影响。
2.
Ag-carrying porous SiO2 as a new kind of inorganic antibacterial materials was prepared.
探讨了以多孔SiO2为载体的含银无机抗菌剂的制备工艺和灭菌性能。
3.
The large surface area of the resulting SiO2-TiO2 nanocomposites is attributed to the small crystallite size and porous SiO2.
在溶胶-水热法所合成的锐钛矿相TiO2纳米晶基础上,利用模板剂调制的SiO2溶胶进一步合成了多孔SiO2与TiO2复合纳米粒子,重点研究了复合SiO2对纳米锐钛矿相TiO2热稳定性及光催化活性的影响。
3) Ag-carried porous silica
载银多孔SiO2
1.
An Ag-carried porous silica is prepared with absorption method and is characterized by XRD and minimalinhbitory concentration(MIC).
随焙烧温度升高,载银多孔SiO2抗菌性能逐渐降低。
4) nano-porous SiO_2
纳米多孔SiO2
1.
The mechanical property of a nano-porous SiO_2 thin film was determined by this technique.
应用此技术对纳米多孔SiO2薄膜的机械性能进行了测定,当其膜密度为1。
5) porous silica powder
多孔SiO2粉体
6) Ag-carried porous SiO_2
载Ag多孔SiO2
补充资料：多苯基多亚甲基多异氰酸酯
多苯基多亚甲基多异氰酸酯，简称PAPI，或称粗MDI，浅黄色至褐色粘稠液体．有刺激性气味。相对密度(20℃／20 ℃)1．2，燃点218℃。PAPI实际上是由50％MDI与50％官能度大于2以上的多异氰酸酯组成的混合物。升温时能发生自聚作用。溶于氯苯、邻二氯苯、甲苯等。PAPI的活性低，蒸气压低，只是TDI的百分之一，故毒性很低。
用于制造聚氨脂胶粘剂。也可直接加入橡胶胶粘剂中，改善橡胶与尼龙或聚酯线的粘接性能。贮存于阴凉、通风、干燥的库房内，远离火种、热源。严格防水、防潮，避免光照。
用于制造聚氨脂胶粘剂。也可直接加入橡胶胶粘剂中，改善橡胶与尼龙或聚酯线的粘接性能。贮存于阴凉、通风、干燥的库房内，远离火种、热源。严格防水、防潮，避免光照。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。