1) Cr3C2/Ni-base alloy composite layer
Cr3C2/Ni基合金复合涂层
2) Ni-Cr_3C_2 composite coating
Ni-Cr3C2复合涂层
3) Cr3C2-Ni composite coating
Cr3C2-Ni复合涂层
4) FeAlCr/Ni wrapped Cr_3C_2 composite coating
FeAlCr/Ni包Cr3C2复合涂层
1.
THT07-135 high temperature wear machinery was used to analyse tribological properties of high velocity arc sprayed FeAl, Fe-Al/Cr_3C_2, FeAlCr/Ni wrapped Cr_3C_2 composite coatings.
使用THT07 135高温磨损实验机对高速电弧喷涂FeAl,Fe Al/Cr3C2,FeAlCr/Ni包Cr3C2复合涂层进行了滑动摩擦特性的研究,并用SEM、TEM、XRD等手段观察分析了磨痕的形貌和成分、涂层截面的组织和相结构。
5) TiC_p/Ni-base alloy composite layer
TiCp/Ni基合金复合涂层
6) Fe/Cr3C2 composite coating
Fe/Cr3C2复合涂层
1.
Taking 16Mn steel as substrate material,Fe/Cr3C2 composite coating was sprayed on its surface,and aluminum was sprayed on the top of the composite coating by electric arc.
以16Mn钢为基材,在其表面电弧喷涂Fe/Cr3C2复合涂层,再在复合涂层之上再电弧喷涂铝。