1) CNTs-Ag-G composite
碳纳米管-银-石墨复合材料
1.
Effect of pressure on electrical wear of CNTs-Ag-G composites;
外加载荷对碳纳米管-银-石墨复合材料电磨损性能的影响
2.
CNTs-Ag-G composite brushes were fabricated by means of powder metallurgy method.
采用粉末冶金方法制备碳纳米管-银-石墨复合材料,研究了电流密度对碳纳米管-银-石墨复合材料的接触电压降及其磨损性能的影响。
3.
The friction and wear behavior of the CNTs-Ag-G composite sliding against a copper alloy in the presence of electric current was evaluated and compared with that in the absence of the external electric field using a ring-on-block friction and wear tester.
采用粉末冶金方法制备了碳纳米管-银-石墨复合材料,研究了复合材料在机械磨损和带电磨损2种状态下的摩擦磨损性能及接触电压降的变化情况。
2) CNT-Ag-G composite
碳纳米管-银-石墨复合材料
1.
Effect of circular velocity on the contact voltage drop of CNT-Ag-G composite;
圆周速度对碳纳米管-银-石墨复合材料接触电压降的影响
2.
CNT-Ag-G composite brushes were fabricated by means of powder metallurgy.
采用粉末冶金法制备碳纳米管-银-石墨复合材料电接触材料,在带电状态下(10A/cm2),研究了压力对碳纳米管-银-石墨复合材料接触电压降的影响,结果表明:当压力较小时(10N/cm2,5N/cm2),由于电刷的跳动产生火花,导致复合材料接触电压降较大;随压力增加,复合材料电刷和换向器的实际接触面积增大,接触电阻减小,电刷的接触电压降下降;由于碳纳米管的研磨作用,阻止了润滑膜随磨损时间延长而增厚,使电刷的接触电压降维持在一个较稳定的数值上。
3) CNTs/Ag/G composite
碳纳米管/银/石墨复合材料
1.
CNTs/Ag/G composites were prepared by means of powder metallurgical method and the electrical contact properties were examined.
采用粉末冶金法制备碳纳米管/银/石墨复合材料(CNTs/Ag/G),研究了碳纳米管增强银/石墨复合材料的电接触性能。
5) Carbon nanotube/ Carbon composite
碳纳米管/碳复合材料
6) CNTs/C/C composites
纳米碳管/炭/炭复合材料
补充资料：银石墨合金
分子式：
CAS号：
性质：银基含有石墨成分的二元合金。碳在液态银和固态银中溶解度很小。合金中石墨含量一般在2%～5%，有些达到50%，具有良好的导电性、优良的耐磨性和自润滑性、接触电阻低且稳定、抗熔焊不产生氧化膜。有AgC2、AgC5等。银粉和石墨粉均匀混合后，经压制成型和烧结而成。烧结温度为900℃，时间1.5～2.5h。适宜作中等电流的滑动接触元件，如电阻器的滑动部分、转子电刷、空气断路器和航空电器等的接点。
CAS号：
性质：银基含有石墨成分的二元合金。碳在液态银和固态银中溶解度很小。合金中石墨含量一般在2%～5%，有些达到50%，具有良好的导电性、优良的耐磨性和自润滑性、接触电阻低且稳定、抗熔焊不产生氧化膜。有AgC2、AgC5等。银粉和石墨粉均匀混合后，经压制成型和烧结而成。烧结温度为900℃，时间1.5～2.5h。适宜作中等电流的滑动接触元件，如电阻器的滑动部分、转子电刷、空气断路器和航空电器等的接点。