1) Zn-Ni-Sn ternary alloy
Zn-Ni-Sn三元合金
1.
Electroplating Zn-Ni-Sn ternary alloy on electrolyte copper foil using alkaline salt pyrophosphate solution was investigated.
采用碱性焦磷酸盐体系在电解铜箔上电镀Zn-Ni-Sn三元合金可改善铜箔表面的综合性能。
2) Zn-Sn-Ni alloy
Zn-Sn-Ni合金
1.
This dissertation electroplated Zn-Sn and Zn-Sn-Ni alloys by employing alkalescent sulfate-pyrophosphate system on electrolytic copper foil, by optimizing bath composition and composition of compound additives, and employing alkalescent low-chrome bath for passivation and silane coupling agents for closing treatment.
本文采用碱性硫酸盐-焦磷酸盐体系在电解铜箔表面电沉积Zn-Sn及Zn-Sn-Ni合金镀层,选择明胶、胡椒醛、胺类添加剂、十二烷基苯磺酸钠等作为复合添加剂。
3) Cu–Zn–Sn ternary alloy
Cu–Zn–Sn三元合金
1.
Imitation gold plating can produce light lustrous deposits including Cu–Zn binary alloy and Cu–Zn–Sn ternary alloy, and has bright luster.
仿金电镀层包括Cu–Zn二元合金或Cu–Zn–Sn三元合金,色泽鲜艳。
4) Ni-Zn-P alloy
Ni-Zn-P三元合金
1.
Depositing rate of electroless plating Ni-Zn-P alloy;
Ni-Zn-P三元合金沉积速率的研究
5) Zn-Sn alloy
Zn-Sn合金
1.
The combination properties of copper foil surface can be improved by electroplating Zn-Sn alloy on it using alkaline pyrophosphate system.
在电解铜箔上采用碱性焦磷酸盐体系电镀Zn-Sn合金,可改善铜箔表面的综合性能。
6) Sn-Zn alloys
Sn-Zn合金
1.
According to the analysis of the resistivity—temperature(ρ—t) curves,the obtained significant abnormal variation of the(electrical) resistivity at high temperature of Sn-Zn alloys is considered.
采用直流四电极法研究了常压下Sn-Zn合金系的电阻率随温度连续升温的变化规律。
2.
Powders of Sn-Zn alloys with different Zn contents were prepared.
结果表明:固态Sn-Zn合金的氧化产物为SnO2和ZnO,并呈现致密氧化膜的特征;Sn-Zn合金的氧化速率随着Zn含量的增加而加快。
补充资料：Ni-Zn ferrite
分子式：
分子量：
CAS号：
性质：高频软磁铁氧体，具有尖晶石结构，由铁、镍、锌的氧化物及其盐类用陶瓷工艺制成。其电阻率较高，可用到几百兆赫。此材料可制成中频变压器、短波天线棒、磁头、磁芯。还可在高频强磁场下用作发射机终端的级间耦合变压器或质子同步加速器的谐振腔的加速磁体等。
分子量：
CAS号：
性质：高频软磁铁氧体，具有尖晶石结构，由铁、镍、锌的氧化物及其盐类用陶瓷工艺制成。其电阻率较高，可用到几百兆赫。此材料可制成中频变压器、短波天线棒、磁头、磁芯。还可在高频强磁场下用作发射机终端的级间耦合变压器或质子同步加速器的谐振腔的加速磁体等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条