1) anti-hydrolytic property
抗水解
1.
The results show that the nano aluminum nitride powder treated with coupling agent-styrene composite surface treatment agent has excellent anti-hydrolytic property.
结果表明:纳米AlN粉末经偶联剂–苯乙烯接枝进行表面修饰可显著提高其抗水解的能力,室温下长达一个月遇水不发生变化;在70℃的热水浴浸泡24h,其悬浮液pH值仍能保持在7。
2) antihydrolysis
抗水解
1.
Mechanism of antihydrolysis is forming a protecting film of compound of aluminium and the surface treatment agent ZJ 1.
用表面处理剂ＺＪ－１对氮化铝粉末表面进行处理有效地改善了其抗水解性能，在１００℃的沸水中蒸煮４ｈ氮化铝粉末的悬浮液ｐＨ值不随蒸煮时间而改变。
3) hydrolysis resistance
抗水解
1.
In this paper, several methods had been used to improve the hydrolysis resistance of poly butylene terephthalate(PBT).
通过封闭PBT的端羧基 ,使端羧基浓度下降到 10meq/kg以下 ,并且添加抗水解稳定剂 ,消耗水解过程新生的端羧基 ,以减缓PBT的酸性水解速度 ,提高PBT树脂耐水解
2.
Industrial aluminum nitride(AlN) powder was surface modified with organic carboxylic acid and polyethylene glycol (PEG) as surface modifier and the hydrolysis resistance and modifying mechanism of AlN powder before and after modification were studied.
目前,对Al N粉体抗水解性能已有相关研究。
4) resistance to hydrolysis
抗水解性
1.
The results showed that the BE has good resistance to hydrolysis,high surface activity with cmc(0.
以硼酸三乙酯、N-羟甲基丙烯酰胺、N,N-二羟乙基十二烷基胺等为主要原料,合成了新型可聚合非离子硼酸酯表面活性剂(BE),由IR和1HNMR进行表征和确认,并考察了产物的抗水解性、表面活性、均聚合及与丙烯酰胺的共聚合性能。
5) Hydrolytic Resistance
抗水解性能
1.
Effect of Polycarbodiimide on Hydrolytic Resistance of Poly(lactic acid);
聚碳化二亚胺对聚乳酸抗水解性能的影响
6) against hydrolysis treatment
抗水解处理
1.
Research progress on against hydrolysis treatment of AlN powder
AlN粉末抗水解处理的研究进展
补充资料：α-型抗结晶抗絮凝酞菁蓝
分子式：
CAS号：
性质：红光蓝色粉末。属于稳定α-型晶相。具有良好的耐溶剂稳定性。在溶剂中不发生色光与晶型的转变。日晒牢度7～8级。以铜酞菁母体与甲醛缩合，其产物与N-羟甲基苯二甲酰亚胺反应，生成的N-羟甲基苯二甲酰亚胺衍生物与铜酞菁母体以1:10质量比混合，再经酸溶，析出，过滤，漂洗，干燥得最终产物。用于高档油墨、涂料及塑料的着色。
CAS号：
性质：红光蓝色粉末。属于稳定α-型晶相。具有良好的耐溶剂稳定性。在溶剂中不发生色光与晶型的转变。日晒牢度7～8级。以铜酞菁母体与甲醛缩合，其产物与N-羟甲基苯二甲酰亚胺反应，生成的N-羟甲基苯二甲酰亚胺衍生物与铜酞菁母体以1:10质量比混合，再经酸溶，析出，过滤，漂洗，干燥得最终产物。用于高档油墨、涂料及塑料的着色。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条