1) water dissolution
水溶法
1.
Optimization of the water dissolution process for silver brazing fluxes;
银钎焊剂水溶法改性处理工艺的优化
2.
According to the research of water dissolution for copper brazing fluxes,the best project is chosen in the orthogonal test.
通过拟定助焊剂配料方案,在水溶法改性处理工艺上用正交试验法选出铜钎剂的基础实验优化方案,并在优化方案中加入AlPO3以降低钎剂的熔点。
2) water solvent
水溶剂法
1.
The monostearic sucrose ester was synthesized with water solvent, optimal condition sucrose: fatty acid glyceride = 3∶1(mole Ratio); emulsifying agent 5%, catalyst 5%,water 10% (based on the weight of main reactants); reation time 4 h, temperature 150 ℃, vacuum 0.
采用水溶剂法合成蔗糖单硬脂酸酯适宜的反应条件为 :蔗糖与硬脂酸单甘酯摩尔比为 3∶ 1、乳化剂用量5%、催化剂用量 5%、水用量 10 %、反应温度 150℃、反应时间 4 h、压力 0 。
3) aqueous phase
水溶剂法
1.
The optimum reaction conditions via aqueous phase were investigated,and the yield and purity of chlorpyrifos were over 95% and 97% respectively.
以2,3,5,6-四氯吡啶和液碱为原料,一步制得3,5,6-三氯吡啶醇钠,3,5,6-三氯吡啶醇钠和O,O-二乙基硫代磷酰氯反应得到目标产物,报道了一种用三元复合催化剂催化合成毒死蜱的新方法,探讨了采用水溶剂法合成毒死蜱的适宜的工艺条件,毒死蜱的收率、质量分数分别达到95%和97%以上,并采用IR、1H NMR对该化合物的结构进行了表征。
2.
The optimum reaction conditions via aqueous phase were investigated.
本文研究了水溶剂法合成毒死蜱的工艺。
4) aqueous solution method
水溶液法
1.
Oriented ZnO nanorod arrays have been synthesized on a glass slide coated with ZnO thin films using an aqueous solution method.
采用简单的低温水溶液法,在修饰有ZnO种子膜的玻片上制备出形貌规整、取向性较好的ZnO纳米棒阵列。
2.
Highly oriented ZnO nanorod arrays on electrodeposited ZnO-coated seed layers were fabricated by aqueous solution method.
采用水溶液法在电沉积的ZnO种子层上制备了高度取向的ZnO纳米棒阵列,并通过碱溶液化学腐蚀法获得了ZnO纳米管。
5) sol-hydrothermal method
溶胶-水热法
1.
The TiO_2 nanoparticles capped with sodium dodecylbenzenesulfonate(DBS)have been synthesized by a sol-hydrothermal method.
采用溶胶-水热法合成了十二烷基苯磺酸钠(DBS)包覆的TiO_2纳米粒子,分析了溶胶的pH值和DBS用量对包覆效果的影响,并利用IR和TG-DTA对样品进行了表征。
2.
Nanometer-sized TiO_2 and doped nanometer-sized TiO_2 was synthesized via the sol-gel method or sol-hydrothermal method.
用传统的溶胶-凝胶法、改进的溶胶-水热法制备了纳米TiO2和掺杂纳米TiO2,通过对甲基橙有机废水的光催化降解模拟实验,比较不同产品的光催化性能,发现改进的溶胶-水热法优于传统的溶胶-凝胶法,掺杂纳米TiO2优于纯纳米TiO2。
3.
Titania(TiO2) particles were prepared by the sol-hydrothermal method with titanium(Ⅳ) n-butoxide as raw materials and nitric acid aqueous solution as the peptizer.
以钛酸丁酯为原料,以硝酸的水溶液为胶溶剂,采用溶胶-水热法制备了TiO2粒子。
6) Solution mining in caverns
硐室水溶法
补充资料：电解食盐水溶液法
分子式：
CAS号：
性质：制造烧碱(氢氧化钠)和氯气的重要方法。将食盐溶解、净化，配成饱和溶液加入电解槽中。通直流电后产生离子的迁移和放电。溶液中的阴离子(氯离子或氢氧离子)移向阳极而放电，阳离子(钠离子和氯离子)移向阴极而放电。在阳极生成氯气，在阴极生成烧碱溶液和氯气。烧碱溶液经过蒸发、浓缩可制得液体烧碱(液碱)和固体烧碱(固碱)。此法所用电解槽有隔膜式的、离子膜式的和水银电解槽。由于烧碱、氯气、氢气和氯气加工的产品用途广泛，此电解食盐溶液为起点，已经形成具有较大规模的氯碱工业。
CAS号：
性质：制造烧碱(氢氧化钠)和氯气的重要方法。将食盐溶解、净化，配成饱和溶液加入电解槽中。通直流电后产生离子的迁移和放电。溶液中的阴离子(氯离子或氢氧离子)移向阳极而放电，阳离子(钠离子和氯离子)移向阴极而放电。在阳极生成氯气，在阴极生成烧碱溶液和氯气。烧碱溶液经过蒸发、浓缩可制得液体烧碱(液碱)和固体烧碱(固碱)。此法所用电解槽有隔膜式的、离子膜式的和水银电解槽。由于烧碱、氯气、氢气和氯气加工的产品用途广泛，此电解食盐溶液为起点，已经形成具有较大规模的氯碱工业。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条