1) phenolic resin based carbon fibers
酚醛基炭纤维
2) carbon fiber/phenolic
炭纤维/酚醛
1.
Compressive properties and failure mechanism of three dimensional and five directional carbon fiber/phenolic braided composites;
三维五向炭纤维/酚醛编织复合材料的压缩性能及破坏机制
3) Phenolic resin based activated carbon fiber
酚醛基活性炭纤维
1.
Phenolic resin based activated carbon fibers (ACF-H2O) prepared using steam activation at 800 ℃ were investigated by means of N2 adsorption, AC impedance and constant current discharge techniques.
利用水蒸汽活化法制备了酚醛基活性炭纤维(ACF-H2O),对其比表面积、孔结构与在LiClO4/PC(聚碳酸丙烯酯)有机电解液中的电容性能之间的关系进行了探讨。
4) Phenolic resin based carbobn fiber
酚醛树脂基炭纤维
5) novoloid-based carbon fiber
酚醛基碳纤维
6) phenolic fibers
酚醛纤维
1.
The curing reaction of phenolic fibers;
用固化反应法制备酚醛纤维
2.
This result is a help to chioce of the way of the disengaging PVA from phenolic fibers.
通过IR分析 ,确定了酚醛纤维纺丝过程中未与载体PVA发生化学交联 ,两者的联接方式为物理混合。
3.
Phenolic fibers modified by epichlorohydrin were prepared.
在酚醛树脂的合成过程中引入环氧氯丙烷,通过聚合反应得到改性酚醛树脂,以此为原料,采用熔融纺丝法制备出环氧氯丙烷改性酚醛纤维。
补充资料：酚醛基活性碳纤维
分子式：
CAS号：
性质：酚醛碳纤维经活化而得的活性碳纤维。直径9～11μm。比表面积1500～2500m2/g。外表面积1.0～1.2m2/g。微孔径1.5～3.5nm。强度294～392MPa。模量9.8～14.7GPa。苯吸收率30％～80％。甲基蓝吸附性310～380ml/R。制法将酚醛纤维在惰性气体保护下于900℃通入含氧水蒸气或CO2而得。用途有溶剂回收、有害气体吸附、除臭、卫生材料、空气净化、创伤绷带、电极材料、隔膜分离器、电敏元件防护罩、特殊防护服等。
CAS号：
性质：酚醛碳纤维经活化而得的活性碳纤维。直径9～11μm。比表面积1500～2500m2/g。外表面积1.0～1.2m2/g。微孔径1.5～3.5nm。强度294～392MPa。模量9.8～14.7GPa。苯吸收率30％～80％。甲基蓝吸附性310～380ml/R。制法将酚醛纤维在惰性气体保护下于900℃通入含氧水蒸气或CO2而得。用途有溶剂回收、有害气体吸附、除臭、卫生材料、空气净化、创伤绷带、电极材料、隔膜分离器、电敏元件防护罩、特殊防护服等。