1) quenched-in nuclei
淬态核
2) As-cast Quenching
铸态淬火
3) quenched state
快淬态
4) quenched-in crystals
淬态相
1.
The results indicated that the as-cast Nd60Fe20Al10Ni10-xYx(x=0,2) amorphous alloys were fabricated with some quenched-in crystals which could be restrained by Y.
结果表明,淬火态的Nd60Fe20Al10Ni10-xYx(x=0,2)合金基本为非晶组织同时还含有少量的淬态相,Y的加入抑制了淬态相的析出。
2.
The quenched-in crystals are usually found in the sample with a diameter of larger than 10 mm when it is made in vacuum lower than 10-3 Pa and starting materials purity lower than 99.
9%的情况下,当制备样品直径大于10 m m时,经常发现非晶基体中含有一定数量的淬态相,该相的数量不在X衍射仪检测范围内,同时D SC分析表明,这些淬态相对非晶合金的过冷液相区、晶化温度和玻璃转变温度影响也较小。
5) liquid metal quenching
液态淬火
6) as cast ribbon
淬态薄带
1.
5B 9 as cast ribbon prepared with quenching speed V=30m/s is about -22.
通过调高Cu在合金薄带的含量 ,并采用合适的甩带速度V ,在FeCuNbSiB淬态薄带材料中观察到了较大的巨磁阻抗效应。