1) Ni-P/Ni-B double layer composite coating
Ni-P/Ni-B双层复合合金镀层
1.
The operation method,the craft condition and main functions of Ni-P/Ni-B double layer composite coating on aluminium alloy by electroless plating are researched.
为了解决雷达波导管内表面既具有优良导电性能又耐臭氧腐蚀的技术要求,对铝合金化学镀Ni-P/Ni-B双层复合合金镀层的操作方法、工艺条件及主要性能进行了研究,结果表明,若用Ni-P/Ni-B化学镀层替代电镀银层,导电性能有所降低,而耐臭氧腐蚀性能明显增强。
2) Ni-P/Ni-B double composite plating
Ni-P/Ni-B双层复合镀
1.
The process flow and applications of electroless Ni-P alloy, Ni-W-P ternary alloy, Ni-P/Ni-B double composite plating and Ni-P-particle composite plating on aluminum alloy were summarized.
本文分析了铝合金化学镀的特点,综述了铝合金化学镀Ni-P合金、Ni-W-P等三元合金、Ni-P/Ni-B双层复合镀及Ni-P-微粒化学复合镀的工艺流程及应用。
3) Ni-P-TiO2 composite coating
Ni-P-TiO2复合镀层
4) Ni-P-SiO2 Composite Deposits
Ni-P-SiO_2复合镀层
5) Ni-P-SiC Composite Coating
Ni-P-SiC复合镀层
1.
The Ni-P plating and Ni-P-SiC composite coating were prepared using electroless deposite method on the surface of low-alloy cast iron.
作者利用化学沉积法在低合金铸铁表面分别制取了Ni-P镀层和Ni-P-SiC复合镀层,并就两者的耐磨性与铸铁、磷化处理表面及Cr镀层的进行了对比试验研究。
2.
Ni-P-SiC composite coating was prepared by brush plating so as to improve the properties of Ni-P alloy coating.
为了改善Ni-P-SiC复合镀层的性能,采用电刷镀技术制备了复合镀层。
6) SiCp /Ni-P composite coating
SiCp/Ni-P复合镀层
补充资料：1-Hydroxymethyl-3-ni-trobenzen
分子式：C7H7NO3
分子量：153.14
CAS号：619-25-0
性质：针状结晶。熔点32℃，沸点175-180℃（0.4kPa），120-125℃（6.65×10-3kPa）。不溶于水。
制备方法：将2.0g硼氢化钾和2ml2mol/L氢氧化钠配成18ml水溶液，在搅拌下滴加到100ml甲醇和15.1g间硝基苯甲醛的混合物中，控制在18-25℃反应。然后加入稀硫酸酸化，从反应液中蒸除甲醇，用乙醚提取，提取液经洗涤干燥后蒸除乙醚，减压蒸馏，收集183-185℃（2.26kPa）馏分，得13g间硝基苄醇。
用途：有机合成中间体。
分子量：153.14
CAS号：619-25-0
性质：针状结晶。熔点32℃，沸点175-180℃（0.4kPa），120-125℃（6.65×10-3kPa）。不溶于水。
制备方法：将2.0g硼氢化钾和2ml2mol/L氢氧化钠配成18ml水溶液，在搅拌下滴加到100ml甲醇和15.1g间硝基苯甲醛的混合物中，控制在18-25℃反应。然后加入稀硫酸酸化，从反应液中蒸除甲醇，用乙醚提取，提取液经洗涤干燥后蒸除乙醚，减压蒸馏，收集183-185℃（2.26kPa）馏分，得13g间硝基苄醇。
用途：有机合成中间体。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条