2) Sn-Zr oxide
Sn-Zr氧化物
3) Zr-Sn-Nb alloy
Zr-Sn-Nb合金
1.
The specimens of Zr-Sn-Nb alloy with two different composition were treated in different ways as 1 000 ℃-0.
将两种Zr-Sn-Nb合金样品分别进行1000℃-0。
2.
Hot-rolling, cold-rolling and quenching tests of Zr-Sn-Nb alloy were carried out at 750℃, 780℃, 800℃ and 820℃, respectively.
对Zr-Sn-Nb合金在4种温度(750℃、780℃、800℃和820℃)下进行了热/冷加工和最终再结晶退火,并对在上述4种温度下加热的试样进行了淬火处理。
3.
The corrosion products on the I-SCC fracture of Zr-Sn-Nb alloys have been investigated by SEM and EDXA.
利用SEM和EDXA对Zr-Sn-Nb合金碘致应力腐蚀断口上的腐蚀产物进行了观察分析。
4) Zr-Sn-Nb zirconium-based alloy
Zr-Sn-Nb锆合金
5) (Zn,Sn)TiO3 system compounds
(Zr,Sn)TiO_3系化合物
6) Zr-Sn-Nb new zirconium alloys
Zr-Sn-Nb新锆合金
1.
The specimens of Zr-Sn-Nb new zirconium alloys were treated in different ways at 1 045 ℃/40 min+500 ℃/1.
5 h工艺,将Zr-Sn-Nb新锆合金加工成厚度为1。
补充资料：CaO-TiO2-SiO2 ceramics
分子式：
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条