1) silicon nitride-based material
氮化硅基材料
1.
Novel mesostructured silicon nitride-based materials were synthesized for the first time by using acetonitrile as the solvent and octadecylamine as the template in the non-oxide sol-gel process.
以乙腈为溶剂,十八胺为模板剂通过非氧化物溶胶-凝胶过程合成了新颖形貌的氮化硅基材料。
2) silicon nitride-based tool materials
氮化硅基刀具材料
3) silicon nitride based composite ceramics
氮化硅基复合陶瓷材料
4) silicon carbide fiber reinforced Si3N4-matrix composite
碳化硅纤维补强氮化硅基复合材料
5) silicon nitride composite
氮化硅复合材料
1.
Preparation of a kind of particle reinforce silicon nitride composite (Si_3N__(4p)/Si_3N_4 by chemical vapor infiltration (CVI) method was researched in this paper.
本文探索采用化学气相渗透法制备一种颗粒强韧氮化硅复合材料(Si_3N_(4p)/Si_3N_4),研究了颗粒预制体制备工艺和化学气相渗透工艺,并对氮化硅复合材料进行了性能测试与表征。
6) silicon nitride whisker reinforced silicon nitride ceramic
氮化硅晶须补强氮化硅陶瓷基复合材料
补充资料：氮化硅基刀具材料
分子式：
CAS号：
性质：以β-Si3N4为基础加入金属氧化物、碳化物所组成的刀具材料。主要加入碳化钛、氧化铝、氧化钇等。一般密度3.35g/cm3，分解温度1927℃，杨氏模量300GPa，断裂强度830MPa，断裂韧性7.3MPa·m1/2。用于制作加工铸铁、镍基高温合金、硅铝合金等的刀具。
CAS号：
性质：以β-Si3N4为基础加入金属氧化物、碳化物所组成的刀具材料。主要加入碳化钛、氧化铝、氧化钇等。一般密度3.35g/cm3，分解温度1927℃，杨氏模量300GPa，断裂强度830MPa，断裂韧性7.3MPa·m1/2。用于制作加工铸铁、镍基高温合金、硅铝合金等的刀具。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。