1) porous carbon
多孔碳
1.
The characterizations of the porous carbon were determined with mercury porosimetry, scanning electron microscope and BET surface analyzer.
采用液相聚合相分离技术制备了多孔碳,并用压汞仪、BET比表面仪及扫描电镜对多孔碳性能进行表征。
2.
The Sn/PC composite material was prepared by adopting porous carbon material with porous structure and high specific surface area as matrix in order to improve the cycling property of tin anode with high reversible specific capacity for Li ion battery.
为了改善锂离子蓄电池中高比容量锡负极的循环性能 ,采用多孔结构、高比表面积的多孔碳材料为载体制备得到Sn/PC复合材料。
3.
Porous carbon materials with a high surface area and a hierarchical porous network have been prepared from rice straws.
本文研究以常见的生物质材料──玉米秸秆、稻秆、松针和松子壳为原材料,经过简单的碳化和活化处理制备出一系列具有不同比表面积的多孔碳材料。
2) porous carbon plates
多孔碳板
1.
In this task,porous carbon plates are selected as key material in PEMFC humidifier.
本课题选用一种多孔碳板作为增湿器的核心材料,这种多孔碳板密度小、导热性能良好并且在一定压力的作用下允许流体通过。
3) porous SiC
多孔碳化硅
1.
Sample of porous SiC polycrystals are prepared by solid sintering process under high temperature and normal pressure using moulding SiC powder.
碳化硅粉末经压制成型后,在高温常压下固相烧结制成多孔碳化硅样品。
4) porous carbon electrode
多孔碳电极
1.
Cyclic voltammetry, electrochemical impedance spectrometry and potential step were used to test the electrochemical performance of these ionic liquid electrolytes on porous carbon electrode.
制备了数种离子液体及离子液体有机溶液电解质,用线性电位扫描法测试了它们的电化学窗口;并通过循环伏安、交流阻抗、电势阶跃等电化学方法,对它们在多孔碳电极中的电化学性能进行了研究。
5) porous carbon bead
多孔碳小球
6) carbon foam packing
多孔碳填料
补充资料：多孔碳晶须
分子式：
CAS号：
性质：具有多微孔表面的碳晶须。比表面积20.6m2/R，比表面积比2.1～17.8，弯曲强度和模量各为155～208MPa和5.7～6.3GPa。对树脂等基体具有良好的黏合性。制法是将直径0.8μm，平面形状比46，相对密度1.96和比表面积2.58m2/g的气相成长碳晶须，边加热至1000℃边与水蒸气和氮混合气接触而得。用于作塑料、陶瓷、金属和橡胶基复合材料增强剂及层间化合物的晶核等。
CAS号：
性质：具有多微孔表面的碳晶须。比表面积20.6m2/R，比表面积比2.1～17.8，弯曲强度和模量各为155～208MPa和5.7～6.3GPa。对树脂等基体具有良好的黏合性。制法是将直径0.8μm，平面形状比46，相对密度1.96和比表面积2.58m2/g的气相成长碳晶须，边加热至1000℃边与水蒸气和氮混合气接触而得。用于作塑料、陶瓷、金属和橡胶基复合材料增强剂及层间化合物的晶核等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条