1) CZYO
铈锆钇复合氧化
2) complex of ceria and yttria
钇铈复合氧化物
1.
Oxalic acid and ammonium bicarbonate were used as precipitating agents to produce yttrium oxide and complex of ceria and yttria,respectively.
分别用草酸和碳酸氢铵为沉淀剂通过沉淀法制备氧化钇及钇铈复合氧化物,并以其为原料,在高温下合成YAG∶Ce黄色荧光粉。
3) Ceria zirconia mixed oxides
铈锆复合氧化物
1.
In present dissertation, foundational studies on the relation among the preparation method, texture and properties of zirconia and ceria zirconia mixed oxides for automotive catalyst coatwash were carried out.
(3)探索了制备条件对铈锆复合氧化物结构和储氧性能的影响规律。
4) zirconia-ceria mixed oxide
锆铈复合氧化物
5) cerium-zirconium mixed oxide
铈锆复合氧化物
1.
Improving the specific surface area and thermal stability are always hotspots for cerium-zirconium mixed oxides.
铈锆复合氧化物作为助剂应用于三效催化剂引起了人们的广泛关注。
6) Ce_xZr_(1-x)O_2
铈锆复合氧化物
1.
The preparation and characteristic of Ce_xZr_(1-x)O_2 with high specific surface area; 2.
高老化比表面积铈锆复合氧化物的制备及表征；2。
2.
Direct Synthesis of Diethyl Carbonate from CO_2 and Ethanol over Ce_xZr_(1-x)O_2 and CeO_2 Catalysts;
本文对铈锆复合氧化物(CexZr1-xO2)及氧化铈(CeO2)催化二氧化碳和乙醇直接合成碳酸二乙酯进行了研究。
补充资料：氧化锆-氧化钇红外陶瓷
分子式： ZrO2-Y2O3
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。