1) nanosized tetragonal polycrystal zirconia
纳米四方多晶氧化锆
2) nanometer tetragonal polycrystalline zirconia
四方多晶氧化锆
1.
The present work was to determine the optimum sintering system and properties of the nanometer tetragonal polycrystalline zirconia green body by the aqueous gel tape casting process.
采用水基凝胶流延工艺制备四方多晶氧化锆薄膜,确定合理的烧成制度,并考察薄膜的显微结构与烧结性能。
3) tetragonal zirconia polycrystal
四方氧化锆多晶
1.
The microstructure and phases present in hydroxyapatite(HA) reinforced by tetragonal zirconia polycrystal (TZP) were investigated by using transmission electron microscopy(TEM).
用透射电子显微镜对四方氧化锆多晶 (TZP)增韧羟基磷灰石 (HA)复合材料的微观相结构进行了观察与分析 。
4) tetragonal nano-ZrO_2
纳米四方型氧化锆
5) zirconia nanocrystallite
氧化锆纳米晶体
1.
High dispersive and well-defined spherical zirconia nanocrystallites were synthesized by the self-assembly of a cationic surfactant under the hydrothermal conditions.
用阳离子表面活性剂十六烷基三甲基溴化胺(C19H42BrN)进行自组装,在水热条件下合成了高分散、近似球形、均匀粒径的氧化锆纳米晶体。
6) nano-sized ZrO_2 crystal
纳米氧化锆晶体
1.
Preparing nano-sized ZrO_2 crystal in Hydrothermal Method;
水热法制备纳米氧化锆晶体
补充资料：四方氧化锆多晶体
分子式：
CAS号：
性质：由细晶粒的四方相组成的致密氧化锆陶瓷，四方相的稳定剂为氧化钇、氧化铈等。具有高强度韧性，抗弯强度>2GPa，断裂韧性(KIC)>20MPa·m1/2。耐磨性好。硬度高、导热系数低[1300℃时为2.09W/(m·K)]。和铁及铁合金的匹配性良好。采用湿法制粉经单相温度区烧结制取。主要用作砂磨机和球磨机球、抽油泵油阀、医疗用刀具、汽车发动机针阀等。
CAS号：
性质：由细晶粒的四方相组成的致密氧化锆陶瓷，四方相的稳定剂为氧化钇、氧化铈等。具有高强度韧性，抗弯强度>2GPa，断裂韧性(KIC)>20MPa·m1/2。耐磨性好。硬度高、导热系数低[1300℃时为2.09W/(m·K)]。和铁及铁合金的匹配性良好。采用湿法制粉经单相温度区烧结制取。主要用作砂磨机和球磨机球、抽油泵油阀、医疗用刀具、汽车发动机针阀等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。