1) TiCl4 hydrolisis process
TiCl4水解法
2) hydrolysis of TiCl_(4)
TiCl4水解
1.
Nanostructured TiO_(2) thin films were fabricated on glass substrates by soaking the substrates in and (lifting) the substrates from TiO_(2) colloids prepared via the hydrolysis of TiCl_(4).
以TiCl4水解法,采用浸渍提拉法在玻璃片上制备TiO2纳米薄膜。
3) aqueous TiCl4 solution
TiCl4水溶液
4) TiCl4 oxalic acid process
TiCl4草酸法
1.
The high pure titanium dioxide was prepared,adopting the TiCl4 oxalic acid process and the TiCl4 hydrolisis process.
采取TiCl4草酸法和TiCl4解法制备高纯二氧化钛,比较不同条件下的产品质量,找出最佳生产方案。
5) TiCl_4
TiCl4
1.
Studies on Synthesis of Nanometer TiO_2Thin Film with TiCl_4 as a Precursor;
TiCl4水解在玻璃基质上成功地制备了粒径在20～50nm的锐钛型TiO2薄膜 光催化甲基橙溶液实验测试了TiO2薄膜的光催化活性 实验结果表明:镀膜次数越多,光催化活性越高,当镀膜达5次时,光降解率为92。
6) titanium tetrachloride
TiCl4
1.
This paper researched the process of hydrolysis recycling of still bottoms during purifying TiCl4 in titanium tetrachloride production by chlorination.
研究了氯化法生产四氯化钛中对粗四氯化钛精制产生的蒸馏釜残液进行部分水解后,回收TiCl4的工艺,简要分析了该回收处理工艺的反应机制、特点及关键控制点。
补充资料：低压压热釜油脂水解法
分子式：
CAS号：
性质：早期常用的油脂水解工艺方法。油脂和水在压热釜中通入压力为1MPa的饱和蒸汽。温度达到该压力下的饱和温度(约180℃)。由于在此温度下水在油脂中的溶解度不够，要加入碱性催化剂，一般用钙、镁或锌的氧化物，以氧化锌较普遍。其实质是第一步生成上述碱土金属的皂，金属皂使油脂与水形成油包水型乳液。在上述条件下反应时间为10h左右，分批进行，分解率可达95％。当原料质量好时，所得的脂肪酸色泽浅，不经蒸馏即可直接用于制皂或其他产品。