1) SiAlON-bonded corundum brick
SiAlON结合刚玉砖
1.
Multiple erosion of alkali metals and zinc to SiAlON-bonded corundum bricks for blast furnace;
碱金属和锌对高炉用SiAlON结合刚玉砖的复合侵蚀
2) β-SiAlON bonded corundum brick
β-SiAlON结合刚玉砖
1.
High temperature mechanical properties and microstructure of β-SiAlON bonded corundum bricks;
β-SiAlON结合刚玉砖的高温力学性能与显微结构
3) β-SiAlON-TiN bonded corundum
β-SiAlON-TiN结合刚玉
1.
High temperature mechanical properties of β-SiAlON-TiN bonded corundum composites;
β-SiAlON-TiN结合刚玉复合材料的高温力学性能
4) Sialon bonded corundum refractories
Sialon结合刚玉耐火材料
1.
Rheological behavior and stability of their suspensions of Sialon bonded corundum refractories were investigated, Suspensions with 79vol% exhibit shear-thinning characteristic, especially in 10～100s~(-1), and satisfy gelcasting.
研究了Sialon结合刚玉耐火材料浓悬浮体的流变性能和稳定性能。
5) Rebonded corundum brick
再结合刚玉砖
1.
Rebonded corundum brick made from sintered corundum;
用烧结刚玉研制再结合刚玉砖
6) Sialon bonded corundum bricks
赛隆结合刚玉砖
1.
Sialon bonded corundum bricks are produced using silicon, alumina and brown fused corundum as main starting materials in a flowing nitrogen atmosphere.
以工业硅粉、氧化铝和棕刚玉为主要原料 ,在氮化炉内烧成 ,生产了赛隆结合刚玉砖 ,其指标和性能达到和超过法国某公司同类产品 ,满足了武钢 1号高炉使用要
补充资料：电熔再结合刚玉砖
分子式：
CAS号：
性质：又称熔粒刚玉砖。以电熔刚玉为原料，采用烧结法制成的耐火砖。氧化铝含量大于90％，主要矿物组成为刚玉。耐火度约为2000℃。荷重软化温度较高，一般在1550℃以上。常温耐压强度600MPa以上。耐热震性比熔铸刚玉砖好。对酸性或碱性炉渣或含碱的玻璃液都有一定的抵抗能力。生产方法与高铝质制品的相似，先将刚玉熔块破碎后进行拣选、除铁，然后进行配料、混合和成型。难烧结，需在高于1800℃的高温下烧成。也可以加入适当的结合剂制成不烧制品。可用于玻璃熔窑和其他高温窑炉中条件苛刻的部位。
CAS号：
性质：又称熔粒刚玉砖。以电熔刚玉为原料，采用烧结法制成的耐火砖。氧化铝含量大于90％，主要矿物组成为刚玉。耐火度约为2000℃。荷重软化温度较高，一般在1550℃以上。常温耐压强度600MPa以上。耐热震性比熔铸刚玉砖好。对酸性或碱性炉渣或含碱的玻璃液都有一定的抵抗能力。生产方法与高铝质制品的相似，先将刚玉熔块破碎后进行拣选、除铁，然后进行配料、混合和成型。难烧结，需在高于1800℃的高温下烧成。也可以加入适当的结合剂制成不烧制品。可用于玻璃熔窑和其他高温窑炉中条件苛刻的部位。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条