1) Sr-ferrite oxysome materials of high intrinsic coercivity
高内禀矫顽力锶铁氧体
1.
This paper discusses the methods of obtaining Sr-ferrite oxysome materials of high intrinsic coercivity by using high-purity Fe2O3 and SrCO3 as raw materials and CaCO3, SiO2, and LaCO as additives, and by controlling the molar ratio of the raw materials, the amount of the additives and the particle size of powder.
探讨了以高纯度Fe2O3、SrCO3作原料,采用CaCO3、SiO2、Cr2O3、LaCo等作 添加物,通过控制成分的摩尔比、添加物的加入量、细磨粒度等工艺技术条件,获得 高内禀矫顽力锶铁氧体的方法。
2) intrinsic coercivity
内禀矫顽力
1.
03 ) 7 permanent magnets with high Cu, low Fe, fit Zr, little z had room temperature intrinsic coercivity H ci 1?830.
0 3) 7永磁体的室温内禀矫顽力Hci为 183 0 。
2.
The high intrinsic coercivity Nd10.
0)的增加使粘结磁体的内禀矫顽力JHc线性增加,每0。
3.
The highest room temperature intrinsic coercivity iHc is achieved at more than 2 400 kA/m for z=7.
合金z值对内禀矫顽力温度系数影响显著,其中z=6。
3) intrinsic coercive field
内禀矫顽力
1.
The relation between the remanence and the intrinsic coercive field of periodic and quasi-periodic configuration Sm-Co/α-Fe multilayers and thickness and layer-number of the system are investigated by using the micromagnetic theory.
利用微磁学理论,研究了周期及准周期结构Sm-Co/-αFe交换耦合多层膜体系的剩磁、内禀矫顽力与体系厚度及层数的关系。
2.
To forecast the magnetism of hard/soft exchange-coupling bilayers, the relation between the intrinsic coercive field of the bilayers and the angle between orientation of magnetic field and easy axes of hard layer was investigated by using three-dimension dynamic model based on micromagnetic theory.
微磁学理论为基础,采用三维动力学模型研究了Sm-Co/α-Fe双层膜的内禀矫顽力与外场取向的关系,以预测交换耦合双层膜(硬磁层和软磁层)磁性体系的磁性。
4) intrinsic coercive force
内禀矫顽力
1.
XRD results show that the intrinsic coercive force of annealed powders sharply increases.
结果表明,球磨后再退火处理的磁粉内禀矫顽力大幅提高:球磨时间越长,退火后的内禀矫顽力越高。
2.
By adjusting the formula,adding additives,adopting reasonable technique,permanent ferrite magnets with intrinsic coercive force of 380kA/m were developed,which eliminates the demagnetization at low temperature,and have satisfied the needs of the starting motor of automobile.
用在汽车启动电机上的永磁铁氧体材料需有高内禀矫顽力ＨＣＪ，通过配方调整，添加附加成分，采用合理的工艺，制得的永磁铁氧体内禀矫顽力达３８０ｋＡ／ｍ ，杜绝了低温退磁现象，满足了汽车启动电机的需
5) intrinsic coercivity
内禀矫顽性
6) high coercivity
高矫顽力
1.
Ba ferrite films with high coercivity and large squareness for perpendicular magnetic recording;
高矫顽力和大矩形比钡铁氧体垂直磁记录薄膜
2.
Application of pulsed field technique to magnetic property measurements of rare earth based hard magnetic materials with high coercivity
脉冲磁场技术在高矫顽力稀土永磁测量领域的应用
补充资料：认知内驱力
认知内驱力
cognitive drive
认知内驱力(eognitive drive)当个体想理解要掌握的知识、要阐明与解决问题时所产生的以求知为目标的动机因素。它是成就动机的构成因素之一。大多是从好奇的倾向与探究、操作、领会以及应付环境等有关的心理因素中派生出来的。例如，儿童很早就开始探索自身周围的世界，在新异的景象和声音的刺激下会有特别敏感的反应。经常摆弄、考察玩具和身边的其他小东西，并不断提出“为什么”等问题，这都是好奇心与探究的表现。它的产生不是自生的，主要是获得的，也有赖于特定的学习经验。好奇心与探究的倾向性仅仅是潜在的、非真实的动机因素，还没有特定的内容和方向。潜在的动机力量只有通过个体的实践不断取得成功，才能真正表现出来，才能具有特定的方向。认知内驱力与学习之间的关系是互惠的，它对学习起推动作用，学习的成果又会转而增强认知内驱力。它在有意义的学习中是一种最重要的和最稳定的动机。这种动机指向学习任务本身，满足它的“奖励”是由学习本身提供的，因而又被称为内部动机。教育的主要职责之一是要让学生对获得有价值的知识本身发生兴趣，不是让他们为各种外来的奖励所左右。教育心理学家越来越强调以“了解和理解”激发进一步学习的动机的价值，越来越重视这种内部动机在课堂学习中的头等重要作用。 (赵欣坤撰成立夫审)