1) Dynamic and static back roller mill
动静压支承轧辊轧机
2) hydrostatic-backing mill
静压支承轧机
1.
This paper deals with the vibration signal analysis for a large L/D ratio and openingnonequiareal three-oil-groove of a hydrostatic-backing mill.
对一开式大长径比不等面积三油腔静压支承轧机进行了振动信号分析,分别给出了垂直振动,扭振的测试方法,对不同供油压力下的振动进行了频谱分析,最后根据振动信号讨论了新型轧机的振动特性。
3) hot rolling backup roll
热轧支承辊
1.
Aiming at short service life of hot rolling backup roll after excess of hour angle increment and surfacing in Pangang Steel and the actuality that there have no mature surfacing materials for supporting roll in china,developing welding wire PRJ225,using it on supporting roll with flux 107 and appropriate surfacing technology.
6万吨,超过了目前国内其它钢铁公司热轧支承辊堆焊修复后的过钢量,居国内领先水平。
2.
The shedding reason of hot rolling backup roll shoulder is the existed casting defect.
热轧支承辊脱肩的原因是有铸造缺陷。
4) cold rolling back-up roll
冷轧支承辊
1.
According to the service environment of the cold rolling back-up roller, YJ012–S was selected as intermediate material and YJ243–S fluxed-cored wire was used as surfacing material.
依据窄带不锈钢冷轧支承辊使用工况,选择了YJ012–S堆焊过渡层和YJ243–S药芯焊丝作为堆焊工作层并辅以焊前预热和焊后回火热处理的自动埋弧堆焊工艺对冷轧支承辊进行堆焊修复。
2.
According to the service performance of the cold rolling back-up roll, YJ012-S was chosen as intermediate material and YJ243-S fluxed-cored wires was chosen as surfacing material.
本文依据窄带不锈钢冷轧支承辊使用工况,选择了YJ012-S堆焊过渡层和YJ243-S药芯焊丝作为堆焊工作层并辅以焊前预热和焊后回火热处理的自动埋弧堆焊工艺对冷轧支承辊进行堆焊修复。
5) 4100mm wide plate mill backup roll
4100mm 宽厚板轧机支承辊
6) Backup roil.,backup; bearing ; support
支承，支撑，轧辊
补充资料：斜轧机轧辊
斜轧机轧辊
roll of skew rolling mill
x iezhali zhagun斜轧机轧辊(roll of skew rolling mill)管坯斜轧穿孔(见管坯穿扎)和管材针札延伸时使用的主要变形工具。斜轧使用的轧辊形状有如图所示的桶形、锥形和盘形。二辊曼氏穿孔机三辊穿孔机、三辊轧管机、一般二辊斜轧延伸机、均整机和回转定径机使用桶形轧辊(各轧机轧辊辊面形状不一样);菌式穿孔机、改进型狄舍尔轧机和斜轧热扩径机等使用锥形轧辊;盘形轧辊已很少使用，仅用于斜轧穿孔机。誉 斜轧机轧辊的形状 l一捅形轧辊;2一锥形礼辊;3一盘形轧辊 轧辊的特征尺寸是辊子最大直径、辊身长度和辊子辊面进出口锥角a;和a2。表示轧辊轴线与轧制线在垂直平面内相对位置的特征角是占和叔见图)，占角称为展轧角，在水平平面内是a，称为前进角，两者都可以调整。轧辊最大直径由轧制管坯规格、轧辊强度以及变形区尺寸、咬入条件、轧制速度、电能消耗、轧辊重车次数等工艺要求决定。辊身长度取决于变形区长度的需要。al角大小取决于咬入条件和毛管质量。a:角主要取决于扩径量和毛管内外表面质量。 斜轧机轧辊结构有两种:一种是整体的;另一种是辊轴与辊身分开的，装配时采用红装加键;这样辊轴不会由于辊身报废而废掉。辊轴要选用较好的材料制成. 锥形辊由于轴向分速度与管子轴向运动速度相一致，导致变形均匀，利于改善产品质量，同时可提轧制速度，故得到了发展。 (李连诗)