1) ramie noil fiber
苎麻落麻纤维
1.
The surface of ramie noil fibers was treated by methyl methacrylate and acrylonitrile grafting modification, silicane coupling agent A-151 coupling and polyvinyl chloride(PVC) encapsulating, etc.
采用甲基丙烯酸甲酯、丙烯腈接枝 ,硅烷偶联剂 (A - 15 1)偶联 ,聚氯乙烯 (PVC)包覆等方法对苎麻落麻纤维进行表面处理 ;测试了处理前后落麻纤维的吸水率、单丝强度及其与环氧树脂 (EP)、酚醛树脂 (PF)和不饱和聚酯(UP)等的接触角 ;观察了偶联和包覆后落麻纤维的表面状况 ;选取偶联和包覆后的落麻纤维制备了UP/落麻毡和PP/落麻纤维复合材料 ,测试了其拉伸和弯曲性能并观察了处理前后复合材料的拉伸断面形貌。
2) ramie
[英]['ræmi] [美]['ræmɪ]
苎麻纤维
1.
Graft copolymerization of TDI onto ramie fibers has been studied using ramie yarn and mercerized degummed ramie as starting materials.
以苎麻麻纱和精干麻为原料,研究了甲苯-2,4-二异氰酸酯(TD I)与苎麻纤维的接枝反应,对反应条件进行了初步探讨。
2.
The graft copolymerization of TDI onto ramie fibers has been studied using raw ramie,ramie yarn,ramie rope and ramie fabric as starting materials,the TDI grafting ramie fiber reinforced PE composite was prepared.
以苎麻原麻、纱线、苎麻粗绳、苎麻布为原料,用甲苯-2,4-二异氰酸酯(TDI)进行接枝改性,然后制备出不同苎麻纤维与树脂PE的复合材料。
3.
The characteristics of ramie and bamboo fiber were introduced.
介绍了苎麻纤维和竹纤维的性能特点,通过工艺试验,分析了纤维性能、纺纱工艺等影响纱线质量的因素,探讨了提高苎麻纤维和竹纤维及棉混纺高支纱质量的技术措施。
3) ramie fiber
苎麻纤维
1.
Study on Chemical Grafting Modification of Ramie Fiber;
苎麻纤维化学接枝改性的研究
2.
Dyeing properties of acid dyestuffs on cationic ramie fiber;
阳离子改性苎麻纤维酸性染料染色性能
3.
Process and properties of ramie fiber treated with cationic modification agent SA
阳离子改性剂SA对苎麻纤维的改性工艺及其性能影响
4) ramine fiber
苎麻纤维
1.
Ramine fiber was treated with sodium periodate and the weight loss,structure and mechanical properties of ramine fiber under different treating conditions was investigated.
采用高碘酸钠对苎麻纤维进行处理,研究了不同处理条件下苎麻纤维的失重率、结构及力学性能的变化。
5) ramie fibre
苎麻纤维
1.
Property research of modified ramie fibre;
改性苎麻纤维的性能研究
2.
Effects of accelerated thermal aging on properties of ramie fibre/polypropylene composites
加速热老化对苎麻纤维/聚丙烯复合材料性能的影响
3.
The degradable composite was made by ramie fibre and poly(propylene carbonate) .
采用苎麻纤维和聚碳酸亚丙酯制备了可降解复合材料,讨论了苎麻长度、含量对苎麻/聚碳酸亚丙酯复合材料机械性能的影响,并借助扫描电子显微镜对复合材料的冲击断口形貌进行了观察。
6) ramie Fibers
苎麻纤维
1.
Graft copolymerization of itaconic acid onto ramie fibers was studied with ammonium persulfate as initrictor.
以过硫酸铵为引发剂,使衣康酸与苎麻纤维接枝共聚,对反应条件进行了探讨,并对接枝纤维对金属离子的吸附性能进行了初步研究。
补充资料：麻纤维
| 麻纤维 bast fibre and leaf fibre 从各种麻类植物取得的纤维，包括一年生或多年生草本双子叶植物皮层的韧皮纤维和单子叶植物的叶纤维。韧皮纤维作物主要有苎麻、黄麻、青麻、大麻、亚麻、罗布麻和槿麻等。其中麻、亚麻、罗布麻等胞壁不木质化，纤维的粗细长短同棉相近，可作纺织原料，织成各种凉爽的细麻布、夏布，也可与棉、毛、丝或化纤混纺；黄麻、槿麻等韧皮纤维胞壁木质化，纤维短，只适宜纺制绳索和包装用麻袋等。叶纤维比韧皮纤维粗硬，只能制做绳索等。麻类作物还可制取化工、药物和造纸的原料。
麻纤维由胶质粘结成片，制取时须除去胶质，使纤维分离，称脱胶。麻和亚麻可分离成单纤维。黄麻纤维短，只能分离成适当大小的纤维束进行纺纱，这种纤维束称工艺纤维。在纺织用的麻纤维中，胶质和其他纤维素伴生物较多，精练后，麻纤维的纤维素含量仍比棉纤维低 。麻纤维的纤维素含量和棉接近 ( 在95％以上 )，亚麻纤维素含量比麻稍低，黄麻和叶纤维等纤维素含量只有70％左右或更少。麻和亚麻纤维胞壁中纤维素大分子的取向度比棉纤维大 ， 结晶度也好，因而麻纤维的强度比棉纤维高，可达 6.5克／旦；伸长率小，只有棉纤维的一半，约 3.5％，比棉纤维脆。麻和亚麻纤维表面平滑 ，较易吸附水分 ，水分向大气中散发的速度较快；纤维较为挺直，不易变形。 |