1) Castables for iron trough
铁沟浇注料
1.
Experiment on slag resistance of Al_(2)O_(3)-SiC-C castables for iron trough strengthened by Sialon in-situ synthesized was carried out with static crucible method.
采用静态坩埚法进行了Sialon增强Al2O3 SiC C铁沟浇注料的抗渣实验。
2.
The paper mainly aims at the unsatisfied status that service life of castables for iron trough has not been greatly improved for decades.
本文针对我国出铁沟浇注料使用寿命长期停滞不前的现状，从热力学出发，利用原位反应机理，通过添加Sialon物质先驱体和改变结合剂系统等手段，制备了性能优良、使用寿命长的原位生成Sialon增强Al_2O_3-SiC-C铁沟料。
3) used main trough castable
用后主沟浇注料
4) Castables
浇注料
1.
The effects of the grain size of fused corundum and amounts of magnesia,cement and silica micropowder as additives on the behavior of linear expansion of the corundum-spinel castables in sintering process were studied.
在750~1450℃的温度下测量了试样的线膨胀率,研究了电熔刚玉粒度、氧化镁、水泥及硅微粉加入量对刚玉-尖晶石质浇注料烧成过程中线膨胀率的影响。
2.
CO resistance of sol-gel bonded castables was studied together with the CO resistance of cement bonded castables.
研究了新型溶胶-凝胶结合耐火浇注料的抗CO侵蚀性能,同时也与传统的水泥结合耐火浇注料进行了对比试验,并从侵蚀前后的表观特征、理化性能和微观结构等多方面探讨了其CO侵蚀作用机理。
3.
Based on the Problems of heat shack rupturing and desquamating of firebricks on trolley of heat treatment furnaces,the technology measures were put forward irrigating trolley liner using castables with high resisting heat shack performance.
针对台车式热处理炉台车衬砖热震断裂脱落问题,提出了采用高抗热震性浇注料进行台车工作衬整体浇注的技术措施,根据热处理炉的实际工作条件,完成了浇注料的研制,并在实际应用中,取得了良好的应用效果。
5) castable refractory
浇注料
1.
The application of the castable refractory in the carbon kiln lining and the way of improving lining service life;
浇注料在炭素回转窑内衬施工中的应用及提高内衬使用寿命的途径
2.
Effect of Heat Treatment Temperature on Properties of Calcined Flint Clay-Bauxite Castable Refractory
热处理温度对焦宝石-铝矾土浇注料性能的影响
3.
The characteristic of castable refractory was advanced by analyzing the service conditions on Water-cooled Beam of heating furnace in this paper.
通过对加热炉水冷梁使用条件的分析,提出了该类浇注料应具有的特点。
6) casting material
浇注料
1.
Research and application of the casting material reinforced by steel fibre;
钢纤维增强浇注料的研究与应用
2.
The synthesis of low relative molecular weight of poly(acrylate sodium)and application of them as dispersant on bauxite-based low-cement casting material were studied.
研究了低相对分子质量的聚丙烯酸钠合成及其作为分散剂在矾土基低水泥浇注料上的应用。
3.
The experience of successful application of new early-strengthening high-aluminium casting material to 650 rolling mill continuous oil combusting pusher-type heating furnace is described in this paper.
阐述了新型早强高铝质浇注料在６５０轧机燃油推钢连续式加热炉上应用的经验。