1) Bi-Pt alloy
Bi-Pt合金
1.
Bi-Pt alloy film for detecting of small inorganic and organic molecules was prepared from a dimethylsulfoxide bath using sweep potential deposition.
1V电势区间内循环扫描,从有机体系中制备得到Bi-Pt合金膜,通过扫描电镜观察,能量色散谱(EDS)和X射线衍射(XRD)分析研究了该膜层的形貌、元素组成及电催化性能。
3) Bi-In alloys
Bi-In合金
1.
The influence of the common condition and rotating magnetic field(RMF)condition on the solidification microstructure of Bi-In alloys is studied.
研究了常规条件和旋转磁场条件下Bi-In合金的凝固组织特性。
4) Bi-Mn alloy
Bi-Mn合金
1.
Effect of induced magnetic field on microstructure and magnetic properties of Bi-Mn alloy;
诱导磁场对Bi-Mn合金微观结构与磁性的影响
2.
Textured structures of MnBi precipitated phase in Bi-Mn alloys solidified in a magnetic field;
Bi-Mn合金中MnBi析出相磁致织构的形成
3.
Effects of static magnetic field on alignment structure of MnBi phase in semi-solidified Bi-Mn alloy;
磁场对Bi-Mn合金两相区中MnBi相定向排列的影响
5) Bi-20.5Te Alloy
Bi-20.5Te合金
6) Sn-Bi alloy
Sn-Bi合金
1.
Reversibility of liquid-liquid transition in Sn-Bi alloys;
Sn-Bi合金熔体可逆液-液结构转变的研究
2.
Effects of Rotating Magnetic Field on Microstructure of Sn-Bi Alloy;
旋转磁场对Sn-Bi合金凝固组织的影响
补充资料：弥散强化Pt-5Rh 合金
分子式：
CAS号：
性质：是以PtRh5合金为基用微细二氧化锆为强化相的低铑高强度结构材料，具有高度定向排列的显微组织，抗蠕变性能大于PtRh40。室温性能：密度20.6g/cm3。.抗拉强度286.4MPa。维氏硬度913.6MPa。伸长率42%。1400℃，100h断裂应力为10.3MPa，是PtRh40的1.52倍。用内氧化和复合加工方法制成片材等。制作玻纤工业用漏板，以及工业和民用玻璃熔化坩埚，供料装置和搅拌器等。
CAS号：
性质：是以PtRh5合金为基用微细二氧化锆为强化相的低铑高强度结构材料，具有高度定向排列的显微组织，抗蠕变性能大于PtRh40。室温性能：密度20.6g/cm3。.抗拉强度286.4MPa。维氏硬度913.6MPa。伸长率42%。1400℃，100h断裂应力为10.3MPa，是PtRh40的1.52倍。用内氧化和复合加工方法制成片材等。制作玻纤工业用漏板，以及工业和民用玻璃熔化坩埚，供料装置和搅拌器等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。