1) wire feeding process
喂线处理
1.
Basic proposes and factual effects of cored wire feeding process for cast steel melt, technical parameters and variety of alloys used in the process were introduced .
介绍了铸钢钢液喂线处理的基本目的、喂线处理的实际效果、喂线处理用合金种类及喂线处理工艺参数等 ,指出对铸钢钢液进行喂线处理可以有效降低钢中硫、氧含量 ,降低钢中非金属夹杂物总量 ,改变残留非金属夹杂物形态 ,并提高处理合金的收得率等。
2) cored wire injection process
喂线处理法
3) cored-wire injection nodularizing process
喂丝球化处理法
1.
The cored-wire injection nodularizing process and its key techniques were described including: composition and preparation of cored-wire,cored-wire injection equipment and nodularizing treatment station.
列举了在两家大型企业的应用实例,指出采用喂丝球化处理必须注意的事项,探讨了喂丝球化处理法的优点,说明这种球化处理法是值得推广的球化处理新工艺,有望成为进入我国球化处理第四阶段的标志。
4) Feeding CaSi Wire-Adding RE Treatment
喂CaSi-加RE处理
1.
Effect of Feeding CaSi Wire-Adding RE Treatment on Inclusion and Impact Toughness of Atmosphere Corrosion Resisting Steel 09CuPTiRE;
喂CaSi-加RE处理对耐候钢09CuPTiRE夹杂物和冲击韧性的影响
5) wire feeding
喂线
1.
The results of the rare earth alloy wire feeding process into ladle for 25 t converter at Jinan Iron and Steel Co.
济钢２５ｔ转炉钢包喂稀土合金线的工艺试验结果表明，钢包采用喂线工艺加入稀土合金能明显提高稀土的回收率，平均能达到３６。
2.
The four important problems with regard to wire feeding technology,which are the argon blowing before and after feeding,the feeding speed and the horizontal position of penetration are discussed.
通过对喂线工艺的前吹氩、插入的水平位置、喂线速度及后吹氩四个问题的探讨，推导出前吹氩环流时间，气泡柱最大直径，喂铝线与喂硅钙线的喂线速度，后净化时防卷渣的最大吹氩量等方程式；并针对工业生产的实际需要，提出喂线技术的上述四个问题的工艺操作参数。
3.
This paper describes that the wire feeding technique for producing free cutting steels and alloy steels can replace powder injection.
本文阐明了用喂线代替喷粉精炼易切削钢和合金钢时，同样能改变夹杂物形态和改善钢水流动性，能进一步提高合金元素回收率，降低生产成本，从而获得更好的冶金效果和经济效益。
6) watering area
喂水处
补充资料：帘线表面活化处理
分子式：
CAS号：
性质：在聚酯纤维的纺丝过程牛进行表面活化处理，活化剂有封闭异氰酸酯、环氧树脂、油酸酯等。经活化处理的帘线织成帘布，采用一浴法浸渍液处理后即可得到良好的黏合效果。
CAS号：
性质：在聚酯纤维的纺丝过程牛进行表面活化处理，活化剂有封闭异氰酸酯、环氧树脂、油酸酯等。经活化处理的帘线织成帘布，采用一浴法浸渍液处理后即可得到良好的黏合效果。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条