1) Cr12 High Alloy Steel
Cr12系列高合金钢
1.
Discard of Cr12 High Alloy Steel Forgings by Over Roasting;
Cr12系列高合金钢锻件过烧废品的产生
2) Cr12-series steel
Cr12系列钢
3) Cr12 steel
Cr12钢
1.
Application of boronizing Cr12 steel in drawing die;
Cr12钢渗硼拉深凹模的应用
2.
Depth profile analysis of boronizing layer on Cr12 steel by glow discharge optical emission spectrometry;
辉光放电光谱仪逐层分析Cr12钢表面渗硼层
3.
The punch used for motor silicon steel punching is usually made of Cr12 steel,and its heat treatment process is quenching and low temperature tempering.
一般电机硅钢片冲裁用凸模采用Cr12钢制造,热处理工艺是淬火+低温回火。
5) high alloy steel
高合金钢
1.
photoelectric spectroanalysis for multielement determination of high alloy steel;
高合金钢中的多元素光电光谱测定
2.
Although root over-burn of high alloy steel welding lines is not defined as defect by welding regulations,it significantly affects the life of welded pipes.
高合金钢焊缝根部的"过烧"虽然未被相关焊接规程定义为缺陷,但实际上对焊接管道的使用寿命有极大的影响。
3.
It is serious for embrittlement of high alloy steel carbonitriding and it is difficult to eliminate by low temperature tempering,for example,after quenching and 150℃ 3h tempering,the reductions of area of 20Cr2Ni4A and 18CrNiWA steels in carbonitriding are 10% and 6 4% respectively of those heating in air.
研究了碳氮共渗时的氢脆及其消除方法 ,发现高合金钢氢脆敏感性大 ,在一般低温回火中很难消除 ,如淬火后经 15 0℃×3h回火 ,2 0Cr2Ni4A和 18CrNiWA钢的断面收缩率在碳氮共渗时分别为空气加热的 10 %及 6 4%。
6) Cr12 Steel
Cr12型钢
1.
Video-Detecting and Image-Processing the Structure of Cr12 Steel and Hot Working Processes;
Cr12型钢检测分析及热加工技术
补充资料：高合金钢
分子式：
分子量：
CAS号：
性质：合金元素的总含量一般在10%以上的合金钢。可用于制造使用温度高于600℃的化工设备。
分子量：
CAS号：
性质：合金元素的总含量一般在10%以上的合金钢。可用于制造使用温度高于600℃的化工设备。