1) heat forming
热镦成形
1.
Regarding heat forming process of 1Cr18Ni9Ti as typical forging process, this paper studied the law of various technological parameters on 1Cr18Ni9Ti by means of Gleeble-1500 Thermo-simulation machine and metal-scope.
以 1Cr18Ni9Ti奥氏体不锈钢热镦粗锻造工艺为例 ,通过Gleeble— 150 0热模拟试验机和金相显微镜等手段 ,研究了工艺参数对 1Cr18Ni9Ti热镦成形的影响 ,结果表明 :温度、应变速率、变形程度对热镦成形过程的流动应力和变形后试件的晶粒大小、硬度具有明显的影响规律 ,对于控制奥氏体不锈钢的锻造性能具有重要的指导意
2) upsetting-extrusion forming
镦挤成形
1.
Numerical simulation of restrained split-flow in upsetting-extrusion forming of cylinder gear;
圆柱齿轮镦挤成形约束分流的数值模拟
3) upsetting process
镦粗成形
1.
Coupled thermo-mechanical FEM analysis of the sintered powder during upsetting process;
粉末烧结体镦粗成形过程热力耦合有限元分析
4) electric upsetting
电镦成形
1.
Research on some key techniques of coupled thermo-mechanical FEM simulation for electric upsetting process;
电镦成形过程电热力耦合有限元模拟若干关键技术的处理
5) cold heading forming
冷镦成形
6) forming in final heading
终镦成形
补充资料：自动冷镦机、多工位螺栓自动冷镦机
| |||||||
主要参数内容 | 国际先进 | 国内先进 | 国内一般 | 国内落后 | 评定方法及说明 | ||
（一）加工精度 | 参照GB9166-88、JB/T3053-91 | ||||||
1、冲头夹持器模孔中心线对夹持器后支承面的垂直度（mm） 在100长度上 | 0.008 | 0.01 | 0.015 | ＞0.015 | |||
2、凹模座模孔中心线对凹模后座支承面的垂直度（mm） 在100长度上 | 0.008 | 0.01 | 0.015 | ＞0.015 | |||
3、冲头夹持器模孔中心线对滑块行程的平行度（mm） 在100行程上 | 0.016 | 0.02 | 0.02 | ＞0.02 | |||
4、滑块行程对机身上与凹模座贴合的垂直面的垂直度（mm） 在100行程上 | 0.016 | 0.02 | 0.02 | ＞0.02 | |||
5、工件头部对工件杆部中心线的偏移量（mm） | ＜0.20 | 0.20~0.25 | 0.25~0.30 | ＞0.30 | |||
（二）生产率（件/分） | |||||||
20mm | ＞80 | 70 | 65 | ＜65 | |||
30mm | ＞60 | 50 | 45 | ＜45 | |||
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条