1) particle size of WC
WC粒度
2) WC particle size
WC颗粒粒度
1.
It was summarized that the influence of WC particle kinds, WC particle content, WC particle size on the wear-resisting property of WC reinforced metal matrix composite and some preparation methods of WC reinforced metal matrix composite were also introduced.
综述了WC颗粒种类、WC颗粒粒度、百分含量等对WC颗粒增强复合材料耐磨性能的影响研究现状以及常用的WC颗粒增强材料的制备技术。
3) WC grain size
WC晶粒梯度
4) uniformity of WC particles
WC粒度均匀性
1.
The results of experiments and analysis show that the mean bending strength ( σ m) of the cemented carbide is related to the particle size and uniformity of WC particles.
试验和分析结果表明 :硬质合金的抗弯强度与材料中WC的粒度和粒度均匀性有关 ,σm 的平均值随材料中WC颗粒平均尺寸d的增大而减小 ,随WC粒度均匀性变好而增大。
5) coarse-grained WC
粗颗粒WC
1.
Research is made on the process for production of high-quality coarse-grained WC.
进行了在钨粉碳化阶段添加活性催化剂生产优质粗颗粒WC的工艺研究。
6) WC particles
WC颗粒
1.
WC/GCr15 steel (27%WCp) composite was produced by electroslag melting and casting using bigger WC particles as raw reinforcements.
选择大颗粒WC作增强相 ,采用电冶熔铸工艺制备了含 2 7%WC粒子的WC GCr15钢复合材料 ,观察了复合材料中WC颗粒与钢基体的结合情况 ;在MM 2 0 0型摩擦磨损试验机上研究了室温下复合材料同GCr15钢对摩时的摩擦磨损性能。
2.
The result shows that WC particles are partly melted in the steel phase.
用电冶熔铸的工艺方法制备了含40%WC颗粒的WC/钢复合材料。
补充资料：WC-TiC-Co hard alloy
分子式：
CAS号：
性质：又称钨钛钴合金或YT合金。碳化钨、碳化钛和金属钴组成的合金。按碳化钛含量，可分为高钛(25％～40％)、中钛(10％～20％)和低钛(4％～6％)三类合金。它比碳化钨钴合金具有较高的抗氧化性，硬度和耐磨性，而抗弯强度、冲击韧性等则有所降低。主要用作切削加工钢材的工具。
CAS号：
性质：又称钨钛钴合金或YT合金。碳化钨、碳化钛和金属钴组成的合金。按碳化钛含量，可分为高钛(25％～40％)、中钛(10％～20％)和低钛(4％～6％)三类合金。它比碳化钨钴合金具有较高的抗氧化性，硬度和耐磨性，而抗弯强度、冲击韧性等则有所降低。主要用作切削加工钢材的工具。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条