1) high temperature deformation
高温形变
1.
The various structure characteristies of the high temperature deformation and the recrystallization in W9Mo3Cr4V steel have been studied.
研究了W9Mo3Cr4V钢高温形变再结晶的各种组织特征。
2) high temperature deformation
高温变形
1.
Lubrication action of pure aluminum during high temperature deformation of heat-resistant aluminum alloy;
纯铝在耐热铝合金高温变形过程中的润滑作用
2.
Study on the high temperature deformation mechanism of Ti-15-3 alloy;
Ti-15-3合金高温变形机制分析
3.
Dynamic recrystallization of vanadium microalloyed low carbon steel during high temperature deformation;
钒微合金化低碳钢高温变形动态再结晶
4) hot deformation
高温变形
1.
Research on the constitutive equation of Al_(18)B_4O_(33)w/AZ91D composite during hot deformation;
Al_(18)B_4O_(33)w/AZ91D复合材料高温变形力学本构方程研究
2.
Hot Deformation Behavior of Dual Phase Stainless Steel 00Cr21Ni2Mn5N;
00Cr21Ni2Mn5N双相不锈钢的高温变形
3.
The result indicates that the hot deformation of the ma.
结果表明,该材料在高温变形时的稳态流变应力与应变速率、变形温度均满足Arrhenius方程,其中更满足双曲正弦函数关系;该材料的热变形是受热激活控制的塑性变形过程。
5) hot deformation
热变形，高温变形
补充资料：弹性形变
分子式：
分子量：
CAS号：
性质：弹性材料在外力作用下发生形变后，当外力释去时，形变完全恢复、此种形变称为弹性形变。一般金属材料弹性形变不超过1%，应力应变之间关系符合虎克定律。对非晶态高聚物材料，弹性形变则包括普弹形变和高弹形变两类。普弹形变很小(约0.1-0.2%)，应力应变之间关系符合虎克定律，高弹形变可高达百分之几百。高弹形变是高聚物一种独特的力学特性质，是由处于高弹态的高聚物分子内链段的聚向和位移产生的，形变时内应力小、模量小，形度值很大，当外力除支后可完全恢复。
分子量：
CAS号：
性质：弹性材料在外力作用下发生形变后，当外力释去时，形变完全恢复、此种形变称为弹性形变。一般金属材料弹性形变不超过1%，应力应变之间关系符合虎克定律。对非晶态高聚物材料，弹性形变则包括普弹形变和高弹形变两类。普弹形变很小(约0.1-0.2%)，应力应变之间关系符合虎克定律，高弹形变可高达百分之几百。高弹形变是高聚物一种独特的力学特性质，是由处于高弹态的高聚物分子内链段的聚向和位移产生的，形变时内应力小、模量小，形度值很大，当外力除支后可完全恢复。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。