1) low temperature salt bath chromizing
低温盐浴渗铬
1.
The results showed that a chromized layer with good wear resistance could be gained in steel 45 by low temperature salt bath chromizing.
研究了 45钢低温盐浴渗铬工艺 ,分析了渗铬层的金相组织和相结构 ,测量了渗层厚度、渗层硬度及铬浓度分布 ,并进行了渗铬层的耐磨试验。
2.
The microstructure ,phase make up,chromium thickness,microhardness and corroding resistance of low temperature salt bath chromizing layers of steel Q235,45 and T10 are contrasted.
通过 Q2 35钢、45钢、T1 0钢低温盐浴渗铬层的金相组织、相结构、厚度、铬浓度、显微硬度和耐蚀性的对比 ,表明碳含量越高 ,铬碳化合物层越厚 ,显微硬度越高 ,耐蚀性越好。
3.
Immediate quenching and tempering process of steel T10 after low temperature salt bath chromizing was studied.
研究了 T10钢在低温盐浴渗铬后直接淬火并回火工艺。
2) salt-bath chromizing
盐浴渗铬
1.
Effect of salt-bath chromizing process on microstructure and properties of chromized layer;
T12钢盐浴渗铬工艺对渗层组织和性能的影响
2.
Effects on 45 & T10A steel in different process time of salt-bath chromizing adding rare-earth were studied.
在相同温度下,对45钢和T10A钢进行不同时间的稀土盐浴渗铬,结果表明:随着渗铬时间的延长,渗铬的效果,在总体上呈增加的趋势,45钢在4h就可以达到较好效果,而T10A钢则在6h达到较好效果。
3) low temperature salt-bath
低温盐浴
1.
The technological process of die steel H13 was inguired by low temperature salt-bath vanadium-nitrocarburizing,and microstructures,hardness,element distribution and phases of the infiltration of samples were investigated.
探讨了H13模具钢的低温盐浴氮碳钒共渗工艺,并对渗层组织、硬度、渗层中的元素分布以及物相组成等进行了研究。
4) low temperature chromizing
低温渗铬
6) VANADIZING IN THE SALT BATH WITH LOW CONTENT OF BORAX
低硼砂盐浴渗钒
补充资料：低温离子渗硫
低温离子渗硫
精密离子均匀轰击
1、低温离子渗硫
在 20 世纪八十年代，材料物理学家张弋飞在世界上首先发现，固体硫蒸气产生辉光放电的效应，该效应使金属零件在低温下形成固体润滑层—渗硫层。 这就是著名的“低温离子渗硫”，它的全称是金属表面形成硫化物层的方法和设备，获得了 中、英、德、法、瑞、意、日等多国专利。
至1997年底，低温离子渗硫专利普通许可21家企业生产，取得广泛的经济效益和社会效益。
国内一些企业和科研单位声称开发出“离子渗硫”、“离子硫化”、“真空等离子渗硫”，或称“国外引进”；三家企业被北京市中院判决侵权，一家被宣告实用新型专利无效；见侵权维权
实际上，离子渗硫只有一个能达到120微米渗层深度发明专利，，即“金属表面形成硫化物层的方法和设备”专利。