1) crack of billet
铸坯内部裂纹
1.
Conformation,inclusions and organization of A36 layered cut-side sample have been ana-lyzed with XL-30 SEM and EDS, The results show that the crack of billet which create from inclusions, especially oxide and silicate, are mostly responsible for the layered cut-side sample.
利用XL-30扫描电镜能谱仪对A36钢板切边分层缺陷的形貌、夹杂物和组织进行分析研究,指出铸 坯内部的氧化物和硅酸盐夹杂引起的铸坯内部裂纹是造成钢板切边分层的主要原因。
2) Slab crack
铸坯裂纹
1.
The reasons of slab crack under unsteady casting were analysed.
分析了非稳态浇注时导致铸坯裂纹产生的原因,通过采取相应的控制措施,降低了非稳态浇注时铸坯裂纹的发生率。
3) side internal crack of casting billets
铸坯边内裂
4) casting billets surface crack
铸坯表面裂纹
5) internal crack
内部裂纹
1.
Study on internal cracks in continuous casting steel slab;
连铸钢板坯内部裂纹的研究
2.
Improvement of internal crack of bloom;
方坯低碳钢内部裂纹缺陷的改善
3.
The interrelation between different hypotheses of the formation mechanism of internal cracks is studied to find out the root causes.
针对连铸方坯的内部裂纹质量缺陷,提出一种基于故障树分析的质量分析和优化控制新方法。
6) inner crack
内部裂纹
1.
The possibility of inner micro crack healing was studied by normalizing 20 steel samples including inner crack one time and once again on the basis of the one of the first time .
通过对含有内部裂纹的20钢试样采取一次加热正火和二次加热正火处理,探讨其内部裂纹愈合的可能性。
2.
The possibility of inner microcrack healing was studied by normalizing the 45 steel samples containing inner crack for one time and two times respectively.
对含有内部裂纹的45钢试样采取了不同温度一次加热正火处理和二次加热正火处理,研究了其内部裂纹愈合的可能性。
3.
Through the analysis of inner crack.
连铸圆坯内部裂纹对轧管有相当大的危害 ,本文对攀钢集团成都钢铁有限责任公司炼钢厂已生产的圆管坯内部裂纹的特征进行了分类说明 ,并根据其特征 ,分析了圆管坯内部裂纹产生的原因 ,提出了控制内部裂纹的具体措施 ,并在实践中取得了明显的效果。
补充资料：衡阳钢管厂水平连铸机生产连铸圆管坯
衡阳钢管厂水平连铸机生产连铸圆管坯
衡阳钢管厂水平连铸机生产连铸圆管坯
说明：补充资料仅用于学习参考，请勿用于其它任何用途。