1) electroetching processes
电腐蚀过程
3) process of layer-after-layer corrosion
层层腐蚀过程
4) overcorrosion
过腐蚀
1.
By means of MET,SEM and EPMA,overcorrosion morphology on the surface of 6063 aluminum extrusion,which often appears during the caustic washing process of pretreatment of anodizing,was observed ,and corrosion products were examined.
运用ＭＥＴ、ＳＥＭ、ＥＰＭＡ等手段观察６０６３铝型材在工业阳极氧化预处理的碱洗过程中表面所出现的过腐蚀形貌，同时对腐蚀产物的成分进行分析，找出产生这种过腐蚀的原因，并对其形成机理进行了探讨。
6) corrosion degree
腐蚀程度
1.
It's extremely important to understand the internal corrosion degree of gas pipeline for oil field safety in production.
根据模糊数学综合评价的基本原理,对天然气管道内腐蚀程度进行综合评价,并通过应用示例验证该方法的可行性。
2.
In this paper methods of fuzzy comprehensive judgement is brought forward to evaluate corrosion degree of injecting pipeline, and calculating steps are also given.
提出了利用模糊综合评判方法对注水管道进行腐蚀程度评价的具体方法 ,并通过应用示例验证了该评价方法的实用
补充资料：电腐蚀
电腐蚀
electroerosion
d IonfUShl电腐蚀(eleetroerosion)由于电火花放电使发电机绝缘材料表面造成烧损和腐蚀的现象。现代大容量透平发电机定子线棒的主绝缘一般采用热固性绝缘材料，热固性材料在运行温度下几乎没有热膨胀，由于振动和其他制造原因的影响，致使定子线棒主绝缘外表面防电晕层与槽壁之间接触不良，存在着局部间隙，当线棒主绝缘与防电晕层结合不紧密时也会存在局部间隙。当间隙的电场强度超过某一数值时，将产生间隙火花放电，致使局部温度升高，有时可高达摄氏几千度，使防电晕层和主绝缘表面受到严重腐蚀或烧损。此外，高压定子线棒在通风槽口和端部出槽口处有可能出现电晕放电，使空气电离而产生臭氧及氮的氧化物，与空气中的水分起化学作用，引起线棒表面防电晕层和主绝缘的腐蚀。 间隙上所受的电压与定子绕组电压、定子线棒尺寸、主绝缘材料和厚度、防电晕层的电阻率和线棒的嵌装工艺等有关。环氧粉云母绝缘的线棒较沥青云母带绝缘的线棒容易产生放电;发电机额定电压越高或线棒在运行中所处的电位越高，间隙上所承受的电压也越高;线棒防电晕层表面和槽壁间的接触电阻越大或接触点间的距离越大，间隙上所受的电压也越高。 防止电腐蚀的主要措施是:改进材料性能和提高工艺水平;改进线棒在槽内的固定方法，以使线棒与槽壁接触紧密可命;定子槽内喷半导体漆，槽内垫条采用半导体材料，采用主绝缘和防电晕层一次热压成型，以消除主绝缘和防电晕层之间的局部间隙;在线棒端部出槽口处采用碳化硅半导体漆的防电晕措施等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条