1) layer of poor chromium and rich silicon
贫铬富硅层
2) Cr-depleted layer
贫铬层
3) poor chrome
贫铬
1.
Lower solution treatment temperature of the raw material made the carbide didn't dissolve completely and distributed along the grain boundary like network,so poor chrome happened near the grain boundary and intercrystalline corrosion is produced.
通过对失效件0Cr18Ni9不锈钢制连接螺栓进行失效分析,得出其断裂原因为原材料固溶处理温度偏低,碳化物未充分溶解,并沿晶界呈网状分布,造成晶界附近贫铬,产生晶间腐蚀。
2.
Lower solution treatment temperature of the raw material made the carbide didn t dissolve completely and distributed along the grain boundary like network,so poor chrome happened near the grain boundary and intercrystalline corrosion is produced.
通过对失效件0Cr18Ni9不锈钢制连接螺栓进行失效分析,得出其断裂原因为原材料固溶处理温度偏低, 碳化物未充分溶解,并沿晶界呈网状分布,造成晶界附近贫铬,产生晶间腐蚀。
4) chromium depletion
贫铬
1.
The chromium depletion at a low-energy boundary segment introduced by twin emission into a random boundary was smaller than that of the original random boundary.
在大角度晶界上形成的局部的低能晶界的贫铬程度明显低于原来的大角度晶界的贫铬程度。
2.
The results showed that nitrogen alloying high purity steels exhibited no chromium depletion at grain boundaries after sensitized heat treatment, and showed mainly general corrosion in boiling 65% HNO 3 solution.
２０％）基本上消除敏化态晶间腐蚀，敏化处理不会引起晶界贫铬；当氮含量不超过０。
5) wealth standard
贫富
1.
From then on,the ancient Chinese social class structure began to change from hierarchy standard to wealth standard.
由此,中国古代社会的阶层结构出现转型,由身份等级制向以财富为标准的贫富转化。
6) Ni-Cr-Si composite coating
镍-铬-硅复合涂层
1.
Laser cladding of Ni-Cr-Si composite coatings were prepared on Ti-5621s alloy.
在Ti-5621s合金表面采用激光熔覆制备了镍-铬-硅复合涂层,分析了涂层的显微组织,测试了涂层的硬度和摩擦学性能。
补充资料：卖富差贫
1.谓对于富人，得钱便予以免除差役;对于穷人，便任意征派劳役。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条