1) the irregularity of eutectic carbides
共晶碳化物不均匀度
1.
As a result,the rolling process under low temprature can improve the irregularity of eutectic carbides and make carbids bcome more finer.
主要研究了终轧温度对D2钢轧材的共晶碳化物不均匀度和碳化物颗粒度的影响,研究表明:低温轧制可以改善D2钢轧材的共晶碳化物不均匀度,并细化了碳化物颗粒度。
2) Carbide Nonuniformity
碳化物不均匀度
1.
Influence of Ingot Type on Carbide Nonuniformity in High Speed Steel Product;
钢锭锭型对高速钢碳化物不均匀度的影响
3) carbide inhomogeneity
碳化物不均匀性
1.
The test results show that the overheating sensitivity will be increased when carbide inhomogeneity exceed the normal,even though GCr15 steel measured the standard by normalizing and spheroidal anneal,its overheating sensitivity is still high.
试验发现碳化物不均匀性超过标准要求时,将增大淬、回火组织的过热敏感性,通过正火、球化退火使之符合标准的GCr15钢,其过热敏感性仍较强。
5) Carbide Uniformity
碳化物均匀化
6) eutectic carbide
共晶碳化物
1.
These structures make the quenching temperature to be rise and the overtemperature structure and the uniformity of eutectic carbide in the steel are the major reasons of quenching crack.
结果表明,由于刨齿轮W18Cr4V钢共晶碳化物不均匀度严重超标,网状碳化物、莱氏体的存在使得淬火加热温度过高,造成组织过热,增加了材料的脆性,降低了刨齿刀的力学性能,导致刨齿刀淬火时产生裂纹。
2.
Results show that, when suitable RE is added into high carbon high speed steel,the austenite and eutectic carbides have been changed.
热处理后,共晶碳化物大部分变成团球状且分布均匀。
3.
After heat treatment, network eutectic carbides of cast Cr12 die steel are changed into nodular and dispersed ones in the matrix.
铸造Cr12模具钢中共晶碳化物呈网状分布于晶界上,且枝晶粗大,经Al-Zn变质处理,共晶组织明显细化,离异共晶数量增多;经热处理后,Cr12模具钢共晶碳化物由网状变为粒状和块状且均匀分布于基体中,同时,硬度有所降低,冲击韧性得到明显提高。
补充资料：碳化硅晶须补强碳化硅陶瓷基复合材料
分子式：
CAS号：
性质：以碳化硅陶瓷为基和以碳化硅晶须为增强剂的新型陶瓷材料。通过晶须的载荷转移、拔出及裂纹偏转作用，获得比普通碳化硅更高的强度和韧性。使用温度达1400℃。是一种重要的高温结构陶瓷。用于燃气轮机叶片等高温部件和耐磨件制造。采用原位生长工艺和烧结工艺制取。
CAS号：
性质：以碳化硅陶瓷为基和以碳化硅晶须为增强剂的新型陶瓷材料。通过晶须的载荷转移、拔出及裂纹偏转作用，获得比普通碳化硅更高的强度和韧性。使用温度达1400℃。是一种重要的高温结构陶瓷。用于燃气轮机叶片等高温部件和耐磨件制造。采用原位生长工艺和烧结工艺制取。