1) PbTiO_3/NiTi composite
PbTiO_3/NiTi复合膜
2) NiTi/Si Composite Membrane
NiTi/Si复合膜
3) NiTi alloy thin film
NiTi合金膜
5) NiTi/PZT composites
NiTi/PZT复合材料
1.
The NiTi/PZT composites have been prepared by the method of depositing ferroelectric ceramics(FC) films on the NiTiSMA coll-rolled foil substrate with the sol-gel routes,and combined with the sintering at 650 ℃.
用溶胶-凝胶法在NiTi形状记忆合金冷轧薄片基体上沉积铁电陶瓷PZT薄膜,再通过650℃烧结处理而得到NiTi/PZT复合材料,采用动态热机械分析方法测试了该复合材料及相同温度时效处理的NiTi形状记忆合金的内耗随温度及振动频率的变化曲线,比较了两种材料内耗曲线特征的差异;通过分析内耗曲线随温度、振动频率变化规律研究了材料的振动响应特性。
6) composite particles of TiC and NiTi
TiC-NiTi复合粉体
1.
The NiTi phase in the composite particles of TiC and NiTi, which are synthesized from the raw materials of Ti powder, Ni powder and active carbon by using the high-temperature salt-melting technology, has good reversible martensitic phase-change behavior, moreover, the temperature of martensitic phase change is basically the same as that of the big-block NiTi material.
以Ti粉、Ni粉和活性炭为原料,用高温熔盐的方法合成的TiC-NiTi复合粉体中的NiTi相不但具有良好的可逆马氏体相变行为,而且马氏体转变相变温度与大块NiTi材料基本相同。
补充资料：复合反渗透膜
分子式：
CAS号：
性质：指超薄致密皮层和支撑层材料不同的反渗透膜。其主要特点是超薄致密层薄，最薄可达30nm；膜表层形态为三维结构，有高约0.4μm，平均直径约0.07μm的突起物，使膜面积增加约一倍；超薄致密层结构的疏松和致密程度可在制膜时调节。这些特点使复合反渗透膜透水量增大，操作压力可降低至0.4～0.8MPa的超低压膜，发展了疏松超薄皮层以截留二价盐离子的纳滤膜，和脱盐率≥99.5％的致密超薄皮层的复合反渗透膜。如以聚砜膜为支撑层，芳香聚酰胺为复合皮层的FT-30膜，已经有了更疏松的NF-70膜，更致密的FT-30SW膜和表层形态不同的ESPA膜等。
CAS号：
性质：指超薄致密皮层和支撑层材料不同的反渗透膜。其主要特点是超薄致密层薄，最薄可达30nm；膜表层形态为三维结构，有高约0.4μm，平均直径约0.07μm的突起物，使膜面积增加约一倍；超薄致密层结构的疏松和致密程度可在制膜时调节。这些特点使复合反渗透膜透水量增大，操作压力可降低至0.4～0.8MPa的超低压膜，发展了疏松超薄皮层以截留二价盐离子的纳滤膜，和脱盐率≥99.5％的致密超薄皮层的复合反渗透膜。如以聚砜膜为支撑层，芳香聚酰胺为复合皮层的FT-30膜，已经有了更疏松的NF-70膜，更致密的FT-30SW膜和表层形态不同的ESPA膜等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条