1) layered lanthanum niobate
层状镧铌酸盐
1.
Zirconia pillared layered lanthanum niobate was prepared by first preswelling HLaNb 2O 7 with n C 6H 13 NH 2, and n C 16 H 33 NH 2, then reacting with zirconyl chloride solution(0.
报道了采用分步交换法首次获得氧化锆柱层状镧铌酸盐 ,并研究了不同胺预支撑对其性能的影响 采用XRD、TEM、比表面测试等方法对所合成的新材料进行了表征 结果表明 ,不同链长的有机胺预支撑对最终获得的氧化锆柱层状镧铌酸盐的层间距有着较大的影响 ,采用较长链长的有机胺预支撑对提高产物的层间距有利 其中由正十六胺预支撑的层状镧铌酸制备的氧化锆柱层状镧铌酸盐具有较大的层间距 (d =1。
2) layered lanthanum titanate
层状镧钛酸盐
1.
A silica pillared layered lanthanum titanate was prepared by first exchanging K 2La 2Ti 3O 10 with n C 6H 13 NH 3Cl, then reacting with octa (3 aminopropylsilasesquioxane), and finally calcinating the obtained product in air to remove the interlayered organics.
本文报道通过先用正己胺盐酸盐水溶液与Ｋ２Ｌａ２Ｔｉ３Ｏ１０发生离子交换得到正己铵离子柱撑的层状镧钛酸盐，然后再与氨基丙基三乙氧基硅烷的正八面体多聚体作用，最后将层间的有机物焙烧分解掉后可得新型氧化硅柱层状镧钛酸盐。
4) layered niobate
层状铌酸
1.
Further calcinating the obtained Cr\+\{3+\} polyhydroxyacetato intercalated niobate in N\-2 at 400℃ for 2h gives rise to the chromia pillared layered niobate.
本文报道先用正丙胺预支撑层状铌酸，然后同氯化四甲铵水溶液进行离子交换，最后再与醋酸铬（ Ⅲ） 水溶液反应可得含铬（ Ⅲ） 聚合离子支撑的层状铌酸。
5) lanthanum niobate
镧铌酸
1.
Amine-pillared lanthanum niobates with different chains length as pillars were characterized with XRD, TG and DSC.
用不同链长的有机胺柱撑镧铌酸,采用X射线衍射、热重、差热等分析方法对合成的各种产物进行表征。
2.
The porous silica-pillared perovskite type lanthanum niobates (Si-HLN) were pr epared by stepwise intercalations of n-hexylamine and oligosiloxane formed from the hydrolysis of 3-aminopropyltriethoxysilane (APES) followed by calcina tion of the intercalated precursors.
用正己胺预支撑层状镧铌酸,以3-丙氨基三乙氧基硅烷为硅源,将其水解后形成的硅聚合体粒子插入到镧铌酸的层间,经焙烧后制成氧化硅柱支撑的多孔性镧铌酸催化剂。
6) lanthanum orthoniobate
正铌酸镧
补充资料：铌酸镧：镱,铒
分子式：LaNbO4:Yb3+,Er3+
CAS号：
性质：白色粉末。在红外线970μm激发下发出绿色荧光，绿峰与红峰强度比为3.0。以氧化镧、五氧化二铌、氧化镱和氧化铒为原料在1350℃经5h灼烧而成。用作荧光粉。
CAS号：
性质：白色粉末。在红外线970μm激发下发出绿色荧光，绿峰与红峰强度比为3.0。以氧化镧、五氧化二铌、氧化镱和氧化铒为原料在1350℃经5h灼烧而成。用作荧光粉。