1) nitric acid leaching
硝酸浸出
1.
Bi -leaching sludge is treated by carbonate co verting -nitric acid leaching - sulfuric acid precipitating process.
采用碳酸盐转型—硝酸浸出—硫酸沉铅工艺处理炼铜烟灰浸铋渣。
2) hydrogen nitrate dipping
硝酸浸渍
1.
Waste actived alumina was regenerated by hydrogen nitrate dipping method and then calcined at certain temperature.
采用稀硝酸浸渍后再进行煅烧处理再生废弃活性氧化铝,从稀硝酸浓度、浸渍时间、两个方面探讨稀硝酸浸渍法对废活性氧化铝性能与结构影响。
3) nitric acid
硝酸浸蚀液
4) weak-acid leaching
微酸浸出
1.
There are still some problems in weak-acid leaching technology selection,leaching liquor preparation and leaching liquor application.
浸出技术是地浸采铀的关键技术之一,在微酸浸出工艺的选择、溶浸液配方与使用方法等方面,尚存在一些问题。
5) sulfuric acid leach
硫酸浸出
1.
The paper,according to the analyzing of lead dross reverberator dust,put forward the new technics indium distilling by sulfuric acid leaching,P204 extraction,sulfuric acid washing,hydrochloric acid reverse extraction,zinc replacement,smelting,electrolysis,casting etc.
研究分析了铅浮渣反射炉烟尘的性质和特点,提出了二段硫酸浸出、P204萃取、硫酸洗涤、盐酸反萃、锌板置换、压团熔铸、电解铸型的提铟新工艺,并进行了全流程的试验研究,明确了各工序的工艺技术条件。
补充资料：氨浸出
氨浸出
ammonia leaching
o「、J Inehu氨浸出(ammonia leaehing)J下J含氨的水溶液作为浸出剂的浸出方法。氨是·种配位体，能与某些金属离子形成配合物(络合物)进入溶液。浸出过程一般通入氧作为氧化剂，氧化被浸出固体物料中的有价组分。氨浸出可在常压或加压下进行。含自然铜、氧化铜或碳酸铜的矿石，可在常压下浸出;而含铜、镍、钻、锌等硫化物精矿，则采用加压氧氨浸出，浸出温度通常为358一373K，氧气压力为0.7一1.4MPa。浸出液经蒸馏除去的氨，可用水吸收后循环使用。氨浸出的优点是能处理含铁高和含碱性脉石的矿物原料，设备的防腐问题容易解决。由于氨具有挥发性，氨浸出需要在密闭反应器内进行。