The influence of F,K,Na on start temperature and initial product of solid phase reaction in high basicity sinter was studied by means of differential thermal analysis(DTA) and X-ray diffraction(XRD).
采用差热分析(DTA)与X射线衍射(XRD)相结合的方法,研究了高碱度烧结矿中F、K、Na对烧结固相反应开始温度与最初形成产物的影响规律,研究结果表明:烧结原料中F、K、Na的存在,促进了烧结固相反应过程中低熔点化合物硅酸钠、铁酸钠、枪晶石的形成,固相反应过程中硅酸钠自702℃,铁酸钠自780℃,枪晶石自900℃开始合成,从而探明了F、K、Na在烧结固相反应过程中的行为规律。
4) reaction temperature
反应温度
1.
Effect of reaction temperature on the product of aromatization reaction of FCC gasoline narrow fraction;
反应温度对催化汽油窄馏分芳构化的研究
2.
Effects of reaction temperature on aromatization of FCC gasoline;
反应温度对催化裂化汽油芳构化的研究
3.
Experimental study on oxidation of NO in ship exhaust by O_3——The effect of reaction temperature and C_2H_4 content;
船舶尾气中NO臭氧氧化研究——反应温度和尾气中碳氢化合物含量的影响
5) temperature response
温度反应
6) reacting temperature
反应温度
1.
The results show that solvent system,reacting temperature,washing agent and washing-leaching times can influence the perticle size of HAP powder.
研究发现 ,溶剂体系、反应温度、凝胶清洗用剂及洗滤次数等对所得的粉体粒度有较大的影响。
补充资料：铂电阻温度表(见电阻温度表)
铂电阻温度表(见电阻温度表)
表。bod旧nZu wendubiao铂电阻温度表见电阻温
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条