1) burning resistance polyether
耐燃聚醚
1.
The synthetic recipe and technique of JH-452R burning resistance polyether were introduced.
介绍了 Ｊ Ｈ—４５２ Ｒ 耐燃聚醚的合成配方及工艺路线，讨论了影响产品性能的主要因
2) flame retarding polyether
阻燃聚醚
3) light resistanf PPE
耐光性聚苯醚
4) flame retardant polyether polyol
阻燃聚醚多元醇
1.
The high reactive flame retardant polyether polyol(HIROL) for polyurethane resin was synthesized by copolymerization of epoxy propane(EP), oxirane(EO), pentabromophenyl glycidyl ether(PBPGE) and glycerol, using BF 3·THF as catalyst.
结果表明 ,当环氧乙烷 /环氧丙烷 /五溴苯基缩水甘油醚摩尔配比为 2∶7∶1时 ,所合成的阻燃聚醚多元醇以质量分数2 3%添入国产 2 5 # PU泡沫材料原料中 ,制得的阻燃PU泡沫材料氧指数为 2 8 5 ;与质量分数为 6 %的甲基膦酸二甲酯复配使用 ,氧指数提高到 32。
2.
The flame retardant polyether polyol(HIROL) containing phosphorus was synthesized with dimethyl phosphite and high reactive chloride polyether polyol(CHIRO) which had chloromethyl group in side chain.
研究了侧链含有氯甲基的高活性氯代聚醚多元醇(CHIROL)与亚膦酸二甲酯钠盐反应,合成高活性含磷阻燃聚醚多元醇(HIROL)的方法。
3.
The new flame retardant polyether polyol was prepared using N,N bis(2 hydroxylethyl) 2,4,6 tribromoaniline as beganning material and 3 (2,4,6 tribromophenoxy)epoxypropane as flame retardant raw material.
着重考察了反应物料比、投料方式、反应时间等因素对阻燃聚醚多元醇物理性质及收率的影响。
5) polycarbonate of halogenatedbisphenol A
耐燃聚碳酸酯
6) flame retardant polyether type of polyurethane
阻燃聚醚型聚氨酯
补充资料：耐燃聚碳酸酯
分子式：
CAS号：
性质：又称阻燃聚碳酸酯或耐燃聚碳酸酯。分子链中含有部分氯代或溴代双酚A碳酸酯型结构的聚合物，常为共聚物或共混物。具有耐热和阻燃特性，但加工性较差。溴代较氯代产品更耐热、耐燃。氯代物软化点250～260℃，而溴代物为350～370％。其他性能与双酚A聚碳酸酯基本相似。由四溴(氯)双酚A与双酚A共聚或四溴双酚A聚碳酸酯低聚物作阻燃剂与普通聚碳酸酯共混制得。加工工艺与聚碳酸酯相似，但温度稍高。适于用做电子、机械、航空、船舶、家电的耐热、耐燃零部件。