1.
The Influence of the quenching and tempering treatment and the different subcritical treatment on microstrcture and property of a high alloy white cast iron was studied.
研究了淬回火和不同的亚临界热处理工艺对高合金白口铸铁组织和性能的影响。
2.
The article on the basis of analyzing the latest research of grinding ball and the condition of the grinding ball used in molybdenum mineral joins the right amount copper and vanadium in the high chromium white cast iron prepares the high alloy white cast iron.
本文在分析磨球材料研究现状的基础上，结合磨钼矿用磨球具体的工况条件，在高铬白口铸铁中加入适量的铜、钒制备高合金白口铸铁。
4) Cr-Mn-Cu alloy white cast iron
铬锰铜合金白口铸铁
1.
The wear resistance of Cr-Mn-Cu alloy white cast iron after heat treatment was studied and compared with that of as-cast Cr-Mn-Cu alloy white cast iron,the wear failure mechanism and microstructure on the wear end surface and nonwear end surface were analyzed.
以铬锰铜合金白口铸铁的铸态材料为对比材料,考察了热处理后的铬锰铜合金白口铸铁材料的耐磨性能,对试验材料的磨损失效机理和磨损端面与无磨损端面的金相组织进行了分析。
2.
The wearing resistance,microstructure,worn surface morphology and hardness change in wearing end-face and non-wearing end-face of Cr-Mn-Cu alloy white cast iron were tested and analyzed.
对铬锰铜合金白口铸铁的耐磨性、无磨损端面及磨损端面的微观组织、磨损形貌及硬度进行了试验和分析。
3.
The erosive-wear resistance of heat treated Cr-Mn-Cu alloy white cast iron was investigated compared with that of as-cast one, and the impact fractures,the erosive-wear resistant failure mechanism and the section metallurgical structure of the test materials were analyzed.
以铸态铬锰铜合金白口铸铁为对比材料,考察了热处理后的铬锰铜合金白口铸铁的抗冲蚀磨损性能,并对试验材料的冲击断口形貌、抗冲蚀磨损失效机理和冲蚀磨损横切面的金相组织进行了分析。
5) forged medium-chromium ally white cast iron
锻造中铬合金白口铸铁
6) Low-chromium alloted white cast lron Grinding balls
低铬合金白口铸铁磨球
补充资料：高铬铸铁
分子式：
CAS号：
性质： 铬含量高的耐蚀耐热白口铸铁。依铬含量的不同，可分为铬含量26％～30％和32％～36％两类铸铁。在1000℃以上的氧化性气氛中，高铬耐热铸铁仍有好的抗氧化能力。有良好的强度以及较好的机械加工性能，但韧性较低，不宜用于温度急变场合。常用来制作加热炉炉底板、炉子传送链的构件等。
CAS号：
性质： 铬含量高的耐蚀耐热白口铸铁。依铬含量的不同，可分为铬含量26％～30％和32％～36％两类铸铁。在1000℃以上的氧化性气氛中，高铬耐热铸铁仍有好的抗氧化能力。有良好的强度以及较好的机械加工性能，但韧性较低，不宜用于温度急变场合。常用来制作加热炉炉底板、炉子传送链的构件等。