1) cooling after forged
锻后冷却
2) controll cooling after forging
锻后控冷
3) cooling after rolling
轧后冷却
1.
Comparing the influences of two different kinds of cooling after rolling on microstructure and properties of ultra strength steel with boron, the bainite + ferrite microstructure could be gained by spray water cooling to 450℃ and then natural cooling to room-temperature, therefore, the high yield strength and tensile strength of the testing steel could be gained.
通过对比两种不同的轧后冷却工艺对汽车用含硼超高强度钢组织与性能的影响,得出此类钢轧制后喷水快速冷却到450℃,然后空冷至室温,可以获得贝氏体+铁素体组织,从而使实验钢获得较高的屈服强度和抗拉强度;而轧制后直接空冷至室温,获得的组织为铁素体+细珠光体+少量贝氏体,实验钢的抗拉强度较前者低260MPa。
4) post cooler
后冷却器
1.
A new opinion on flow sheet selection for post cooler of air compressor was put for- ward in this article.
对空气压缩机后冷却器流程的选择提出了新见解。
5) cooling at the late stage
后期冷却
6) aftercooling
后冷却<能>
补充资料：α型钛合金热锻缓冷组织
α型钛合金热锻缓冷组织
719
说明：补充资料仅用于学习参考，请勿用于其它任何用途。